IS 1570 (Part 5):1985 X04Cr17Ni12Mo2: X04Cr17Ni12Mo2: high alloy, stainless or heat-resisting steel. Specified in IS 1570 (Part 5):1985.

Category: Stainless Steel
Grade Details
GradeIS 1570 (Part 5):1985 X04Cr17Ni12Mo2
Standard IS 1570 (Part 5):1985
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
IS 11169 (Part 2) X04Cr17Ni12Mo2 IS 11169 (Part 2):2023 India No activity yet
IS 6911 X04Cr17Ni12Mo2 IS 6911:1992 India No activity yet
ASTM A959 316H ASTM A959:2011 USA No activity yet
ASTM A959 316Ti ASTM A959:2011 USA No activity yet
ASTM A959 316Cb ASTM A959:2011 USA No activity yet
ASTM A959 316N ASTM A959:2011 USA No activity yet
BS 970 (Part 3) 316S33 BS 970 (Part 3):1991 UK No activity yet
ASTM A240/A240M S31600 ASTM A240/A240M:2025 USA No activity yet
ASTM A240/A240M S31609 ASTM A240/A240M:2025 USA No activity yet
ASTM A240/A240M S31635 ASTM A240/A240M:2025 USA No activity yet
ASTM A240/A240M S31640 ASTM A240/A240M:2025 USA No activity yet
IS 6603 X04Cr17Ni12Mo2 IS 6603:2024 India No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
ASTM A959 SS316 ASTM A959:2011 Strong Match
ASTM A276/A276M S31600 ASTM A276/A276M:2017 Strong Match
ASTM A959 316Ti ASTM A959:2011 Strong Match
ASTM A959 316Cb ASTM A959:2011 Strong Match
ASTM A240/A240M S31600 ASTM A240/A240M:2025 Strong Match
IS 1570 (Part 5) X04Cr17Ni12Mo2Ti IS 1570 (Part 5):1985 Strong Match
ASTM A240/A240M S31609 ASTM A240/A240M:2025 Strong Match
ASTM A959 316H ASTM A959:2011 Strong Match
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn P S Cr Ni Mo
<=0.08 <=1.0 <=2.0 <=0.045 <=0.030 16.0-18.0 10.0-14.0 2.0-3.0
Mechanical Properties
Tensile Strength >=515 MPa
Yield Strength >=205 MPa (0.2 % proof stress)
Elongation >=40% (50 mm)
Hardness <=217 HB; <=95 HRB
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2)

More data from IS 1570 (Part 5):1985

From the standard
Annealed, quenched or solution treated plates, sheets and strips 5 properties
Tensile strength, min
515 MPa
0.2 % proof stress, min
205 MPa
Elongation in 50 mm, min
40%
Brinell hardness, max
217 HB
Rockwell B hardness, max
95 HRB
Source: IS 1570 (Part 5):1985, Table 2
Annealed, quenched or solution treated bars and flats 4 properties
Tensile strength, min
517 MPa
0.2 % proof stress, min
207 MPa
Elongation in 50 mm, min
40%
Reduction of area, min
50%
Source: IS 1570 (Part 5):1985, Table 3
Recommended heat treatment 2 entries
Solution treatment (softening) temperature
1000 to 1150 deg C
Solution treatment quenching medium
water, oil, air
A annealing, S softening, ST solution treatment, Q quenching, T tempering, P patenting.
Source: IS 1570 (Part 5):1985, Table 7

Active IS 1570 (Part 5):1985 X04Cr17Ni12Mo2 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active IS 1570 (Part 5):1985 X04Cr17Ni12Mo2 listings at this time.

Register for Alerts

Buyer RFQs for IS 1570 (Part 5):1985 X04Cr17Ni12Mo2

+ Post an RFQ for this grade

No open buyer requirements for IS 1570 (Part 5):1985 X04Cr17Ni12Mo2 at this time.

Register for Alerts