ASTM A240/A240M S42035 vs ASTM A959 .-

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S42035 (ASTM A240/A240M:2025) and ASTM A959 .- (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S42035 is typically used for pressure vessels and general applications (plate, sheet and strip), while ASTM A959 .- is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A240/A240M S42035 is defined under ASTM International, originating from United States, while ASTM A959 .- is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A240/A240M S42035 vs ASTM A959 .- is a 61.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A240/A240M S42035:
EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
61.7%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property ASTM A240/A240M S42035 ASTM A959 .-
Standard ASTM A240/A240M:2025 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.030
Mn (%) <=1.00 <=1.00
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cr (%) 13.5-15.5 18.0-20.0
Ni (%) 1.0-2.5 <=0.50
Mo (%) 0.2-1.2 Not specified
Ti (%) 0.30-0.50 0.07-0.30
Cb (%) Not specified 0.10-0.60
N (%) Not specified <=0.030
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S42035 ASTM A959 .-
Tensile Strength >=550 MPa Not specified
Yield Strength >=380 MPa Not specified
Elongation >=16% Not specified
Hardness <=180 HB Not specified
Condition Plate, sheet and strip; yield by 0.2 percent offset Not specified
Typical Applications
ASTM A240/A240M S42035
Pressure vessels and general applications (plate, sheet and strip)
ASTM A959 .-
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A240/A240M S42035 Be Substituted With ASTM A959 .-?
ASTM A240/A240M S42035 and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A240/A240M S42035
0 active listings and RFQs →
ASTM A959 .-
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S42035 and ASTM A959 .-?
ASTM A240/A240M S42035 specifies Mo which is not specified for ASTM A959 .-. ASTM A959 .- specifies Cb, N which are not specified for ASTM A240/A240M S42035.
Can ASTM A240/A240M S42035 be substituted with ASTM A959 .-?
ASTM A240/A240M S42035 and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.