ASTM A240/A240M S42035 vs ASTM A959 S42010

Close Alternative — 70.8% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S42035 (ASTM A240/A240M:2025) and ASTM A959 S42010 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S42035 is typically used for pressure vessels and general applications (plate, sheet and strip), while ASTM A959 S42010 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A240/A240M S42035 is defined under ASTM International, originating from United States, while ASTM A959 S42010 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A240/A240M S42035 vs ASTM A959 S42010 is a 70.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 70.8%.

Frequently Compared With ASTM A240/A240M S42035:
EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
70.8%
MECHANICAL MATCH
No shared data
OVERALL
70.8%
Specifications
Property ASTM A240/A240M S42035 ASTM A959 S42010
Standard ASTM A240/A240M:2025 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.08 0.15-0.30
Mn (%) <=1.00 <=1.00
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cr (%) 13.5-15.5 13.5-15.0
Ni (%) 1.0-2.5 0.35-0.85
Mo (%) 0.2-1.2 0.40-0.85
Ti (%) 0.30-0.50 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S42035 ASTM A959 S42010
Tensile Strength >=550 MPa Not specified
Yield Strength >=380 MPa Not specified
Elongation >=16% Not specified
Hardness <=180 HB Not specified
Condition Plate, sheet and strip; yield by 0.2 percent offset Not specified
Typical Applications
ASTM A240/A240M S42035
Pressure vessels and general applications (plate, sheet and strip)
ASTM A959 S42010
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A240/A240M S42035 Be Substituted With ASTM A959 S42010?
ASTM A240/A240M S42035 and ASTM A959 S42010 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A240/A240M S42035
0 active listings and RFQs →
ASTM A959 S42010
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S42035 and ASTM A959 S42010?
ASTM A240/A240M S42035 specifies Ti which is not specified for ASTM A959 S42010.
Can ASTM A240/A240M S42035 be substituted with ASTM A959 S42010?
ASTM A240/A240M S42035 and ASTM A959 S42010 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.