ASTM A240/A240M S43035 vs ASTM A240/A240M S43932

Strong Match — 96.5% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S43035 (ASTM A240/A240M:2025) and ASTM A240/A240M S43932 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S43035 is typically used for pressure vessels and general applications (plate, sheet and strip), while ASTM A240/A240M S43932 is commonly used for pressure vessels and general applications (plate, sheet and strip). ASTM A240/A240M S43035 is defined under ASTM International, originating from United States, while ASTM A240/A240M S43932 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A240/A240M S43035 vs ASTM A240/A240M S43932 is a 94.7% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 96.5%.

Frequently Compared With ASTM A240/A240M S43035:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4845 ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 GOST 5632 06Kh23N28 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
94.7%
MECHANICAL MATCH
100%
OVERALL
96.5%
Specifications
Property ASTM A240/A240M S43035 ASTM A240/A240M S43932
Standard ASTM A240/A240M:2025 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cr (%) 17.0-19.0 17.0-19.0
Ni (%) <=0.50 <=0.50
N (%) <=0.030 <=0.030
Ti (%) <=1.10 Not specified
Al (%) <=0.15 <=0.15
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S43035 ASTM A240/A240M S43932
Tensile Strength >=415 MPa >=415 MPa
Yield Strength >=205 MPa >=205 MPa
Elongation >=22% >=22%
Hardness <=183 HB <=183 HB
Condition Plate, sheet and strip; yield by 0.2 percent offset Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
ASTM A240/A240M S43035
Pressure vessels and general applications (plate, sheet and strip)
ASTM A240/A240M S43932
Pressure vessels and general applications (plate, sheet and strip)
Key Differences
Can ASTM A240/A240M S43035 Be Substituted With ASTM A240/A240M S43932?
ASTM A240/A240M S43035 and ASTM A240/A240M S43932 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S43932 is often considered as a substitute for ASTM A240/A240M S43035 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A240/A240M S43035
0 active listings and RFQs →
ASTM A240/A240M S43932
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S43035 and ASTM A240/A240M S43932?
ASTM A240/A240M S43035 specifies Ti which is not specified for ASTM A240/A240M S43932.
Can ASTM A240/A240M S43035 be substituted with ASTM A240/A240M S43932?
ASTM A240/A240M S43035 and ASTM A240/A240M S43932 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S43932 is often considered as a substitute for ASTM A240/A240M S43035 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.