ASTM A240/A240M:2025 S82012: S82012: duplex (austenitic-ferritic) stainless steel plate, sheet and strip (UNS number, no type name printed). Specified in ASTM A240/A240M:2025.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Mn
P
S
Si
Cr
Ni
Mo
N
Cu
<=0.05
2.00-4.00
<=0.040
<=0.005
<=0.80
19.0-20.5
0.8-1.5
0.10-0.60
0.16-0.26
<=1.00
Mechanical Properties
Tensile Strength
>=700 MPa
Yield Strength
>=500 MPa
Elongation
>=35%
Hardness
<=31 HRC
Condition
t <= 0.187 in. [5.00 mm] (first condition printed); yield by 0.2 percent offset
More data from ASTM A240/A240M:2025
From the standard
Mechanical properties2 condition(s)
Product or thickness
Tensile strength, min (MPa)
Yield strength, min (MPa)
Elongation in 50 mm, min (%)
t <= 0.187 in. [5.00 mm]
700
500
35
t > 0.187 in. [5.00 mm]
650
400
35
Minimum values; yield strength by the 0.2 percent offset method.
Source: ASTM A240/A240M:2025, Table 2
Hardness2 condition(s)
Product or thickness
Brinell HBW, max
Rockwell, max
t <= 0.187 in. [5.00 mm]
-
31 HRC
t > 0.187 in. [5.00 mm]
290
-
Maximum values; either Brinell or Rockwell scale may be used.
Source: ASTM A240/A240M:2025, Table 2
Cold bend1 value
Cold bend angle
not required
Bend tests are not required for chromium steels thicker than 1 in. [25 mm] or for any austenitic or duplex steel regardless of thickness.
Source: ASTM A240/A240M:2025, Table 2