ASTM A276/A276M N08367 vs ASTM A959 N08700

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M N08367 (ASTM A276/A276M:2017) and ASTM A959 N08700 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M N08367 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A959 N08700 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A276/A276M N08367 is defined under ASTM International, originating from United States, while ASTM A959 N08700 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M N08367 vs ASTM A959 N08700 is a 75.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A276/A276M N08367:
GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401 ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
75.6%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property ASTM A276/A276M N08367 ASTM A959 N08700
Standard ASTM A276/A276M:2017 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.04
Mn (%) <=2.00 <=2.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cr (%) 20.0-22.0 19.0-23.0
Ni (%) 23.5-25.5 24.0-26.0
Mo (%) 6.0-7.0 4.3-5.0
N (%) 0.18-0.25 Not specified
Cu (%) <=0.75 <=0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M N08367 ASTM A959 N08700
Tensile Strength >=655 MPa Not specified
Yield Strength >=310 MPa Not specified
Elongation >=30% Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M N08367
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A959 N08700
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A276/A276M N08367 Be Substituted With ASTM A959 N08700?
ASTM A276/A276M N08367 and ASTM A959 N08700 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M N08367
0 active listings and RFQs →
ASTM A959 N08700
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M N08367 and ASTM A959 N08700?
ASTM A276/A276M N08367 specifies N which is not specified for ASTM A959 N08700.
Can ASTM A276/A276M N08367 be substituted with ASTM A959 N08700?
ASTM A276/A276M N08367 and ASTM A959 N08700 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.