Close Alternative — 80.6% match
based on chemical composition and mechanical property overlap.
ASTM A276/A276M N08800 (ASTM A276/A276M:2017) and ASTM A276/A276M N08810 (ASTM A276/A276M:2017) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A276/A276M N08800 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A276/A276M N08810 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished).
ASTM A276/A276M N08800 is defined under ASTM International, originating from United States, while ASTM A276/A276M N08810 is defined under ASTM International, originating from United States.
As per chemical composition, ASTM A276/A276M N08800 vs ASTM A276/A276M N08810 is a 95.8% match.
As per mechanical properties, the match is 50%.
Combined, this makes them a close alternative overall at 80.6%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A276/A276M N08800
ASTM A276/A276M N08810
Tensile Strength
>=515 MPa
>=450 MPa
Yield Strength
>=205 MPa
>=170 MPa
Elongation
>=30%
>=30%
Hardness
<=192 HB
<=192 HB
Condition
Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Typical Applications
ASTM A276/A276M N08800
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A276/A276M N08810
Stainless steel bars and shapes (hot-finished or cold-finished)
Can ASTM A276/A276M N08800 Be Substituted With ASTM A276/A276M N08810?
ASTM A276/A276M N08800 and ASTM A276/A276M N08810 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between ASTM A276/A276M N08800 and ASTM A276/A276M N08810?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M N08800 be substituted with ASTM A276/A276M N08810?
ASTM A276/A276M N08800 and ASTM A276/A276M N08810 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.