ASTM A276/A276M N08800 vs ASTM A959 800H

Strong Match — 95.8% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M N08800 (ASTM A276/A276M:2017) and ASTM A959 800H (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M N08800 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A959 800H is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A276/A276M N08800 is defined under ASTM International, originating from United States, while ASTM A959 800H is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M N08800 vs ASTM A959 800H is a 95.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 95.8%.

Frequently Compared With ASTM A276/A276M N08800:
IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
95.8%
MECHANICAL MATCH
No shared data
OVERALL
95.8%
Specifications
Property ASTM A276/A276M N08800 ASTM A959 800H
Standard ASTM A276/A276M:2017 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.10 0.05-0.10
Mn (%) <=1.50 <=1.50
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.015
Si (%) <=1.00 <=1.00
Cr (%) 19.0-23.0 19.0-23.0
Ni (%) 30.0-35.0 30.0-35.0
Fe (%) >=39.5 >=39.5
Cu (%) <=0.75 <=0.75
Al (%) 0.15-0.60 0.15-0.60
Ti (%) 0.15-0.60 0.15-0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M N08800 ASTM A959 800H
Tensile Strength >=515 MPa Not specified
Yield Strength >=205 MPa Not specified
Elongation >=30% Not specified
Hardness <=192 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M N08800
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A959 800H
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can ASTM A276/A276M N08800 Be Substituted With ASTM A959 800H?
ASTM A276/A276M N08800 and ASTM A959 800H overlap closely enough on chemistry and mechanical properties that ASTM A959 800H is often considered as a substitute for ASTM A276/A276M N08800 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M N08800
0 active listings and RFQs →
ASTM A959 800H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M N08800 and ASTM A959 800H?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M N08800 be substituted with ASTM A959 800H?
ASTM A276/A276M N08800 and ASTM A959 800H overlap closely enough on chemistry and mechanical properties that ASTM A959 800H is often considered as a substitute for ASTM A276/A276M N08800 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.