ASTM A276/A276M:2017 N08926 Steel: Specifications & Listings

ASTM A276/A276M:2017 N08926: N08926: nickel-chromium austenitic alloy (listed with the austenitic grades) bars and shapes (UNS number, no type name printed). Specified in ASTM A276/A276M:2017.

Category: Stainless Steel
Grade Details
GradeASTM A276/A276M:2017 N08926
Standard ASTM A276/A276M:2017
ApplicationsStainless steel bars and shapes (hot-finished or cold-finished)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ASTM A959 N08926 ASTM A959:2011 USA No activity yet
EN 10088-1 X1NiCrMoCuN25-20-7 EN 10088-1:2023 Europe (CEN) No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
ASTM A240/A240M N08926 ASTM A240/A240M:2025 Strong Match
ASTM A959 N08926 ASTM A959:2011 Strong Match
EN 10088-1 X1NiCrMoCuN25-20-7 EN 10088-1:2023 Strong Match
EN 10088-1 X1NiCrMoCuN25-20-7 EN 10088-1:2014 Strong Match
ASTM A959 N08367 ASTM A959:2011 Close Alternative
ASTM A240/A240M N08925 ASTM A240/A240M:2025 Close Alternative
IS 11169 (Part 2) X02Cr17Ni12Mo2 IS 11169 (Part 2):2023 Related Material
IS 11169 (Part 2) X02Cr17Ni12Mo3 IS 11169 (Part 2):2023 Related Material
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Mn P S Si Cr Ni Mo N Cu
<=0.020 <=2.00 <=0.030 <=0.015 <=0.50 19.0-21.0 24.0-26.0 6.0-7.0 0.15-0.25 0.50-1.50
Mechanical Properties
Tensile Strength >=650 MPa
Yield Strength >=295 MPa
Elongation >=35%
Hardness <=256 HB
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)

More data from ASTM A276/A276M:2017

From the standard
Mechanical requirements by condition and size 1 row(s)
ConditionFinishDiameter or thickness, in. [mm]Tensile strength, min (MPa)Yield strength, min (MPa)Elongation, min (%)Reduction of area, min (%)Brinell HBW, max
A (Annealed)hot-finished or cold-finishedall65029535-256
Yield by the 0.2 percent offset method. Hardness is HBW unless otherwise indicated; equivalent Rockwell is permitted.
Source: ASTM A276/A276M:2017, Table 2

Active ASTM A276/A276M:2017 N08926 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active ASTM A276/A276M:2017 N08926 listings at this time.

Register for Alerts

Buyer RFQs for ASTM A276/A276M:2017 N08926

+ Post an RFQ for this grade

No open buyer requirements for ASTM A276/A276M:2017 N08926 at this time.

Register for Alerts