ASTM A276/A276M N08926 vs IS 11169 (Part 2) X02Cr17Ni12Mo3

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M N08926 (ASTM A276/A276M:2017) and IS 11169 (Part 2) X02Cr17Ni12Mo3 (IS 11169 (Part 2):2023) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M N08926 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while IS 11169 (Part 2) X02Cr17Ni12Mo3 is commonly used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11). ASTM A276/A276M N08926 is defined under ASTM International, originating from United States, while IS 11169 (Part 2) X02Cr17Ni12Mo3 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A276/A276M N08926 vs IS 11169 (Part 2) X02Cr17Ni12Mo3 is a 61.1% match. As per mechanical properties, the match is 100%. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A276/A276M N08926:
IS 1570 (Part 7) 12Cr13H ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845
Match Breakdown
CHEMISTRY MATCH
61.1%
MECHANICAL MATCH
100%
OVERALL
69.9%
Specifications
Property ASTM A276/A276M N08926 IS 11169 (Part 2) X02Cr17Ni12Mo3
Standard ASTM A276/A276M:2017 IS 11169 (Part 2):2023
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.030
Mn (%) <=2.00 <=2.00
P (%) <=0.030 <=0.045
S (%) <=0.015 <=0.015
Si (%) <=0.50 <=1.00
Cr (%) 19.0-21.0 16.5-18.5
Ni (%) 24.0-26.0 10.5-13.0
Mo (%) 6.0-7.0 2.50-3.00
N (%) 0.15-0.25 <=0.10
Cu (%) 0.50-1.50 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M N08926 IS 11169 (Part 2) X02Cr17Ni12Mo3
Tensile Strength >=650 MPa Not specified
Yield Strength >=295 MPa Not specified
Elongation >=35% Not specified
Hardness <=256 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Reduction of Area, solution annealed (+AT) Not specified >=68% (over 5 to 50 mm)
Tensile Strength, solution annealed (+AT) Not specified <=650 MPa (over 5 to 50 mm)
Typical Applications
ASTM A276/A276M N08926
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 11169 (Part 2) X02Cr17Ni12Mo3
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
Can ASTM A276/A276M N08926 Be Substituted With IS 11169 (Part 2) X02Cr17Ni12Mo3?
ASTM A276/A276M N08926 and IS 11169 (Part 2) X02Cr17Ni12Mo3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M N08926
0 active listings and RFQs →
IS 11169 (Part 2) X02Cr17Ni12Mo3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M N08926 and IS 11169 (Part 2) X02Cr17Ni12Mo3?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M N08926 be substituted with IS 11169 (Part 2) X02Cr17Ni12Mo3?
ASTM A276/A276M N08926 and IS 11169 (Part 2) X02Cr17Ni12Mo3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.