ASTM A276/A276M S20910 vs ASTM A959 XM-19

Strong Match — 94.4% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S20910 (ASTM A276/A276M:2017) and ASTM A959 XM-19 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S20910 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A959 XM-19 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A276/A276M S20910 is defined under ASTM International, originating from United States, while ASTM A959 XM-19 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M S20910 vs ASTM A959 XM-19 is a 94.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 94.4%.

Frequently Compared With ASTM A276/A276M S20910:
EN 10088-1 1.4301 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
94.4%
MECHANICAL MATCH
No shared data
OVERALL
94.4%
Specifications
Property ASTM A276/A276M S20910 ASTM A959 XM-19
Standard ASTM A276/A276M:2017 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.06 <=0.06
Mn (%) 4.0-6.0 4.0-6.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cr (%) 20.5-23.5 20.5-23.5
Ni (%) 11.5-13.5 11.5-13.5
Mo (%) 1.50-3.00 1.50-3.00
N (%) 0.20-0.40 0.20-0.40
V (%) 0.10-0.30 0.10-0.30
Nb (%) 0.10-0.30 Not specified
Cb (%) Not specified 0.10-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S20910 ASTM A959 XM-19
Tensile Strength >=690 MPa Not specified
Yield Strength >=380 MPa Not specified
Elongation >=35% Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S20910
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A959 XM-19
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A276/A276M S20910 Be Substituted With ASTM A959 XM-19?
ASTM A276/A276M S20910 and ASTM A959 XM-19 overlap closely enough on chemistry and mechanical properties that ASTM A959 XM-19 is often considered as a substitute for ASTM A276/A276M S20910 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M S20910
0 active listings and RFQs →
ASTM A959 XM-19
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S20910 and ASTM A959 XM-19?
ASTM A276/A276M S20910 specifies Nb which is not specified for ASTM A959 XM-19. ASTM A959 XM-19 specifies Cb which is not specified for ASTM A276/A276M S20910.
Can ASTM A276/A276M S20910 be substituted with ASTM A959 XM-19?
ASTM A276/A276M S20910 and ASTM A959 XM-19 overlap closely enough on chemistry and mechanical properties that ASTM A959 XM-19 is often considered as a substitute for ASTM A276/A276M S20910 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.