ASTM A276/A276M S20910 vs BS 970 (Part 3) 316S33

Related Material — 59.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S20910 (ASTM A276/A276M:2017) and BS 970 (Part 3) 316S33 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S20910 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while BS 970 (Part 3) 316S33 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; austenitic stainless and heat resisting steel (table 18). ASTM A276/A276M S20910 is defined under ASTM International, originating from United States, while BS 970 (Part 3) 316S33 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, ASTM A276/A276M S20910 vs BS 970 (Part 3) 316S33 is a 59.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 59.9%.

Frequently Compared With ASTM A276/A276M S20910:
EN 10088-1 1.4301 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
59.9%
MECHANICAL MATCH
No shared data
OVERALL
59.9%
Specifications
Property ASTM A276/A276M S20910 BS 970 (Part 3) 316S33
Standard ASTM A276/A276M:2017 BS 970 (Part 3):1991
Category Stainless Steel Stainless Steel
C (%) <=0.06 <=0.07
Mn (%) 4.0-6.0 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Cr (%) 20.5-23.5 16.5-18.5
Ni (%) 11.5-13.5 11.0-14.0
Mo (%) 1.50-3.00 2.50-3.00
N (%) 0.20-0.40 Not specified
V (%) 0.10-0.30 Not specified
Nb (%) 0.10-0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S20910 BS 970 (Part 3) 316S33
Tensile Strength >=690 MPa Not specified
Yield Strength >=380 MPa Not specified
Elongation >=35% Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S20910
Stainless steel bars and shapes (hot-finished or cold-finished)
BS 970 (Part 3) 316S33
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; austenitic stainless and heat resisting steel (Table 18)
Key Differences
Can ASTM A276/A276M S20910 Be Substituted With BS 970 (Part 3) 316S33?
ASTM A276/A276M S20910 and BS 970 (Part 3) 316S33 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S20910
0 active listings and RFQs →
BS 970 (Part 3) 316S33
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S20910 and BS 970 (Part 3) 316S33?
ASTM A276/A276M S20910 specifies N, V, Nb which are not specified for BS 970 (Part 3) 316S33.
Can ASTM A276/A276M S20910 be substituted with BS 970 (Part 3) 316S33?
ASTM A276/A276M S20910 and BS 970 (Part 3) 316S33 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.