ASTM A276/A276M S24000 vs IS 1570 (Part 7) 11Cr17Ni13W3TiH

Minimal Match — 35.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S24000 (ASTM A276/A276M:2017) and IS 1570 (Part 7) 11Cr17Ni13W3TiH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S24000 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while IS 1570 (Part 7) 11Cr17Ni13W3TiH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. ASTM A276/A276M S24000 is defined under ASTM International, originating from United States, while IS 1570 (Part 7) 11Cr17Ni13W3TiH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A276/A276M S24000 vs IS 1570 (Part 7) 11Cr17Ni13W3TiH is a 53.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35.9%.

Frequently Compared With ASTM A276/A276M S24000:
ASTM A959 .- EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
53.9%
MECHANICAL MATCH
0%
OVERALL
35.9%
Specifications
Property ASTM A276/A276M S24000 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Standard ASTM A276/A276M:2017 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) <=0.08 0.07-0.15
Mn (%) 11.5-14.5 <=1.00
P (%) <=0.060 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cr (%) 17.0-19.0 15.5-17.50
Ni (%) 2.3-3.7 12.00-14.50
N (%) 0.20-0.40 Not specified
W (%) Not specified 2.5-3.5
Ti (%) Not specified >=4xC, <=0.80
B (%) Not specified <=0.0006
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S24000 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Tensile Strength >=690 MPa 600-800 MPa
Yield Strength >=380 MPa >=390 MPa (0.2 % proof stress)
Elongation >=30% >=25%
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Bars, forgings, pipes, hot cold worked, thickness up to 60 (first row of Table 3)
Typical Applications
ASTM A276/A276M S24000
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 1570 (Part 7) 11Cr17Ni13W3TiH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can ASTM A276/A276M S24000 Be Substituted With IS 1570 (Part 7) 11Cr17Ni13W3TiH?
ASTM A276/A276M S24000 and IS 1570 (Part 7) 11Cr17Ni13W3TiH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S24000
0 active listings and RFQs →
IS 1570 (Part 7) 11Cr17Ni13W3TiH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S24000 and IS 1570 (Part 7) 11Cr17Ni13W3TiH?
ASTM A276/A276M S24000 specifies N which is not specified for IS 1570 (Part 7) 11Cr17Ni13W3TiH. IS 1570 (Part 7) 11Cr17Ni13W3TiH specifies W, Ti, B which are not specified for ASTM A276/A276M S24000.
Can ASTM A276/A276M S24000 be substituted with IS 1570 (Part 7) 11Cr17Ni13W3TiH?
ASTM A276/A276M S24000 and IS 1570 (Part 7) 11Cr17Ni13W3TiH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.