ASTM A276/A276M:2017 S24000 Steel: Specifications & Listings

ASTM A276/A276M:2017 S24000: S24000 (type XM-29): austenitic stainless steel bars and shapes. Specified in ASTM A276/A276M:2017.

Category: Stainless Steel
Grade Details
GradeASTM A276/A276M:2017 S24000
Standard ASTM A276/A276M:2017
ApplicationsStainless steel bars and shapes (hot-finished or cold-finished)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ASTM A959 XM-29 ASTM A959:2011 USA No activity yet
EN 10088-1 X6CrMnNiN18-13-3 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-3 X6CrMnNiN18-13-3 EN 10088-3:2014 Europe No activity yet
IS 6603 X13Mn13Cr18N IS 6603:2024 India No activity yet
ASTM A276/A276M S24100 ASTM A276/A276M:2017 USA No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
ASTM A959 XM-29 ASTM A959:2011 Strong Match
EN 10088-1 X6CrMnNiN18-13-3 EN 10088-1:2014 Strong Match
EN 10088-1 X6CrMnNiN18-13-3 EN 10088-1:2023 Strong Match
EN 10088-3 X6CrMnNiN18-13-3 EN 10088-3:2014 Strong Match
ASTM A276/A276M S24100 ASTM A276/A276M:2017 Strong Match
IS 6603 X13Mn13Cr18N IS 6603:2024 Strong Match
ASTM A959 XM-28 ASTM A959:2011 Close Alternative
EN 10088-1 X13CrMnNiN18-13-2 EN 10088-1:2014 Close Alternative
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Mn P S Si Cr Ni N
<=0.08 11.5-14.5 <=0.060 <=0.030 <=1.00 17.0-19.0 2.3-3.7 0.20-0.40
Mechanical Properties
Tensile Strength >=690 MPa
Yield Strength >=380 MPa
Elongation >=30%
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)

More data from ASTM A276/A276M:2017

From the standard
Mechanical requirements by condition and size 1 row(s)
ConditionFinishDiameter or thickness, in. [mm]Tensile strength, min (MPa)Yield strength, min (MPa)Elongation, min (%)Reduction of area, min (%)Brinell HBW, max
A (Annealed)hot-finished or cold-finishedall6903803050-
Yield by the 0.2 percent offset method. Hardness is HBW unless otherwise indicated; equivalent Rockwell is permitted.
Source: ASTM A276/A276M:2017, Table 2

Active ASTM A276/A276M:2017 S24000 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active ASTM A276/A276M:2017 S24000 listings at this time.

Register for Alerts

Buyer RFQs for ASTM A276/A276M:2017 S24000

+ Post an RFQ for this grade

No open buyer requirements for ASTM A276/A276M:2017 S24000 at this time.

Register for Alerts