Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
ASTM A276/A276M S28200 (ASTM A276/A276M:2017) and EN 10088-3 X38CrMo14 (EN 10088-3:2014) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A276/A276M S28200 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-3 X38CrMo14 is commonly used for general purposes, semi-finished products, bars, rods, wire, sections and bright products.
ASTM A276/A276M S28200 is defined under ASTM International, originating from United States, while EN 10088-3 X38CrMo14 is defined under European Standard (EN), originating from Europe.
As per chemical composition, ASTM A276/A276M S28200 vs EN 10088-3 X38CrMo14 is a 62.6% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a related material overall at 69.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A276/A276M S28200
EN 10088-3 X38CrMo14
Tensile Strength
>=760 MPa
<=760 MPa
Yield Strength
>=410 MPa
Not specified
Elongation
>=35%
Not specified
Condition
Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, size range not stated; hardness for guidance only
Hardness
Not specified
<=235 HB
Typical Applications
ASTM A276/A276M S28200
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-3 X38CrMo14
General purposes, semi-finished products, bars, rods, wire, sections and bright products
Key Differences
ASTM A276/A276M S28200 specifies N, Cu which are not specified for EN 10088-3 X38CrMo14.
Can ASTM A276/A276M S28200 Be Substituted With EN 10088-3 X38CrMo14?
ASTM A276/A276M S28200 and EN 10088-3 X38CrMo14 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between ASTM A276/A276M S28200 and EN 10088-3 X38CrMo14?
ASTM A276/A276M S28200 specifies N, Cu which are not specified for EN 10088-3 X38CrMo14.
Can ASTM A276/A276M S28200 be substituted with EN 10088-3 X38CrMo14?
ASTM A276/A276M S28200 and EN 10088-3 X38CrMo14 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.