ASTM A276/A276M S30403 vs IS 1570 (Part 5) X02Cr19Ni10

Strong Match — 98.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S30403 (ASTM A276/A276M:2017) and IS 1570 (Part 5) X02Cr19Ni10 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S30403 is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A276/A276M S30403 vs IS 1570 (Part 5) X02Cr19Ni10 is a 98.3% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 98.9%.

Frequently Compared With ASTM A276/A276M S30403:
EN 10088-1 1.4401 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
98.3%
MECHANICAL MATCH
100%
OVERALL
98.9%
Specifications
Property ASTM A276/A276M S30403 IS 1570 (Part 5) X02Cr19Ni10
Standard ASTM A276/A276M:2017 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) <=2.00 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Cr (%) 18.0-20.0 17.5-20.0
Ni (%) 8.0-12.0 8.0-12.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S30403 IS 1570 (Part 5) X02Cr19Ni10
Tensile Strength >=485 MPa >=485 MPa
Yield Strength >=170 MPa >=170 MPa (0.2 % proof stress)
Elongation >=40% >=40% (50 mm)
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Hardness Not specified <=183 HB; <=88 HRB
Typical Applications
ASTM A276/A276M S30403
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 1570 (Part 5) X02Cr19Ni10
Not documented
Can ASTM A276/A276M S30403 Be Substituted With IS 1570 (Part 5) X02Cr19Ni10?
ASTM A276/A276M S30403 and IS 1570 (Part 5) X02Cr19Ni10 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X02Cr19Ni10 is often considered as a substitute for ASTM A276/A276M S30403 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M S30403
0 active listings and RFQs →
IS 1570 (Part 5) X02Cr19Ni10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S30403 and IS 1570 (Part 5) X02Cr19Ni10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S30403 be substituted with IS 1570 (Part 5) X02Cr19Ni10?
ASTM A276/A276M S30403 and IS 1570 (Part 5) X02Cr19Ni10 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X02Cr19Ni10 is often considered as a substitute for ASTM A276/A276M S30403 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.