ASTM A276/A276M S31635 vs IS 1570 (Part 5) X04Cr17Ni12Mo2

Strong Match — 94.7% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S31635 (ASTM A276/A276M:2017) and IS 1570 (Part 5) X04Cr17Ni12Mo2 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S31635 is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X04Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A276/A276M S31635 vs IS 1570 (Part 5) X04Cr17Ni12Mo2 is a 92.1% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 94.7%.

Frequently Compared With ASTM A276/A276M S31635:
IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr13H ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
92.1%
MECHANICAL MATCH
100%
OVERALL
94.7%
Specifications
Property ASTM A276/A276M S31635 IS 1570 (Part 5) X04Cr17Ni12Mo2
Standard ASTM A276/A276M:2017 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Mn (%) <=2.00 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Cr (%) 16.0-18.0 16.0-18.0
Ni (%) 10.0-14.0 10.0-14.0
Mo (%) 2.00-3.00 2.0-3.0
N (%) <=0.10 Not specified
Ti (%) <=0.70 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S31635 IS 1570 (Part 5) X04Cr17Ni12Mo2
Tensile Strength >=515 MPa >=515 MPa
Yield Strength >=205 MPa >=205 MPa (0.2 % proof stress)
Elongation >=40% >=40% (50 mm)
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Hardness Not specified <=217 HB; <=95 HRB
Typical Applications
ASTM A276/A276M S31635
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 1570 (Part 5) X04Cr17Ni12Mo2
Not documented
Key Differences
Can ASTM A276/A276M S31635 Be Substituted With IS 1570 (Part 5) X04Cr17Ni12Mo2?
ASTM A276/A276M S31635 and IS 1570 (Part 5) X04Cr17Ni12Mo2 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X04Cr17Ni12Mo2 is often considered as a substitute for ASTM A276/A276M S31635 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M S31635
0 active listings and RFQs →
IS 1570 (Part 5) X04Cr17Ni12Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S31635 and IS 1570 (Part 5) X04Cr17Ni12Mo2?
ASTM A276/A276M S31635 specifies N, Ti which are not specified for IS 1570 (Part 5) X04Cr17Ni12Mo2.
Can ASTM A276/A276M S31635 be substituted with IS 1570 (Part 5) X04Cr17Ni12Mo2?
ASTM A276/A276M S31635 and IS 1570 (Part 5) X04Cr17Ni12Mo2 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X04Cr17Ni12Mo2 is often considered as a substitute for ASTM A276/A276M S31635 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.