ASTM A276/A276M S31727 vs ASTM A959 S31727

Strong Match — 100% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S31727 (ASTM A276/A276M:2017) and ASTM A959 S31727 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S31727 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A959 S31727 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A276/A276M S31727 is defined under ASTM International, originating from United States, while ASTM A959 S31727 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M S31727 vs ASTM A959 S31727 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With ASTM A276/A276M S31727:
IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property ASTM A276/A276M S31727 ASTM A959 S31727
Standard ASTM A276/A276M:2017 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) <=1.00 <=1.00
P (%) <=0.030 <=0.030
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cr (%) 17.5-19.0 17.5-19.0
Ni (%) 14.5-16.5 14.5-16.5
Mo (%) 3.8-4.5 3.8-4.5
N (%) 0.15-0.21 0.15-0.21
Cu (%) 2.8-4.0 2.8-4.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S31727 ASTM A959 S31727
Tensile Strength >=550 MPa Not specified
Yield Strength >=245 MPa Not specified
Elongation >=35% Not specified
Hardness <=217 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S31727
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A959 S31727
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can ASTM A276/A276M S31727 Be Substituted With ASTM A959 S31727?
ASTM A276/A276M S31727 and ASTM A959 S31727 overlap closely enough on chemistry and mechanical properties that ASTM A959 S31727 is often considered as a substitute for ASTM A276/A276M S31727 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M S31727
0 active listings and RFQs →
ASTM A959 S31727
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S31727 and ASTM A959 S31727?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S31727 be substituted with ASTM A959 S31727?
ASTM A276/A276M S31727 and ASTM A959 S31727 overlap closely enough on chemistry and mechanical properties that ASTM A959 S31727 is often considered as a substitute for ASTM A276/A276M S31727 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.