Close Alternative — 78.9% match
based on chemical composition and mechanical property overlap.
ASTM A276/A276M S32053 (ASTM A276/A276M:2017) and JIS G4304 SUS836L (JIS G4304:2021) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A276/A276M S32053 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while JIS G4304 SUS836L is commonly used for hot-rolled stainless steel plates and strips.
ASTM A276/A276M S32053 is defined under ASTM International, originating from United States, while JIS G4304 SUS836L is defined under Japanese Industrial Standards (JIS), originating from Japan.
As per chemical composition, ASTM A276/A276M S32053 vs JIS G4304 SUS836L is a 80.8% match.
As per mechanical properties, the match is 75%.
Combined, this makes them a close alternative overall at 78.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A276/A276M S32053
JIS G4304 SUS836L
Tensile Strength
>=640 MPa
>=640 MPa
Yield Strength
>=295 MPa
>=275 MPa
Elongation
>=40%
>=40%
Hardness
<=217 HB
<=217 HB
Condition
Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Typical Applications
ASTM A276/A276M S32053
Stainless steel bars and shapes (hot-finished or cold-finished)
JIS G4304 SUS836L
Hot-rolled stainless steel plates and strips
Can ASTM A276/A276M S32053 Be Substituted With JIS G4304 SUS836L?
ASTM A276/A276M S32053 and JIS G4304 SUS836L are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between ASTM A276/A276M S32053 and JIS G4304 SUS836L?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S32053 be substituted with JIS G4304 SUS836L?
ASTM A276/A276M S32053 and JIS G4304 SUS836L are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.