ASTM A276/A276M:2017 S32205 Steel: Specifications & Listings

ASTM A276/A276M:2017 S32205: S32205: austenitic-ferritic (duplex) stainless steel bars and shapes (UNS number, no type name printed). Specified in ASTM A276/A276M:2017.

Category: Stainless Steel
Grade Details
GradeASTM A276/A276M:2017 S32205
Standard ASTM A276/A276M:2017
ApplicationsStainless steel bars and shapes (hot-finished or cold-finished)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ASTM A959 2205 ASTM A959:2011 USA No activity yet
ASTM A240/A240M S32205 ASTM A240/A240M:2025 USA No activity yet
ASTM A959 S31803 ASTM A959:2011 USA No activity yet
EN 10088-1 X2CrNiMoN22-5-3 EN 10088-1:2014 Europe (CEN) No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
ASTM A959 2205 ASTM A959:2011 Strong Match
ASTM A240/A240M S32205 ASTM A240/A240M:2025 Strong Match
ASTM A959 S31803 ASTM A959:2011 Strong Match
EN 10088-1 X2CrNiMoN22-5-3 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrNiMoN22-5-3 EN 10088-1:2023 Strong Match
IS 6603 X02Cr22Ni5Mo3N IS 6603:2024 Close Alternative
ASTM A959 255 ASTM A959:2011 Close Alternative
ASTM A240/A240M S31803 ASTM A240/A240M:2025 Close Alternative
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Mn P S Si Cr Ni Mo N
<=0.030 <=2.00 <=0.030 <=0.020 <=1.00 22.0-23.0 4.5-6.5 3.0-3.5 0.14-0.20
Mechanical Properties
Tensile Strength >=655 MPa
Yield Strength >=450 MPa
Elongation >=25%
Hardness <=290 HB
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)

More data from ASTM A276/A276M:2017

From the standard
Mechanical requirements by condition and size 1 row(s)
ConditionFinishDiameter or thickness, in. [mm]Tensile strength, min (MPa)Yield strength, min (MPa)Elongation, min (%)Reduction of area, min (%)Brinell HBW, max
A (Annealed)hot-finished or cold-finishedall65545025-290
Yield by the 0.2 percent offset method. Hardness is HBW unless otherwise indicated; equivalent Rockwell is permitted.
Source: ASTM A276/A276M:2017, Table 2

Active ASTM A276/A276M:2017 S32205 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active ASTM A276/A276M:2017 S32205 listings at this time.

Register for Alerts

Buyer RFQs for ASTM A276/A276M:2017 S32205

+ Post an RFQ for this grade

No open buyer requirements for ASTM A276/A276M:2017 S32205 at this time.

Register for Alerts