ASTM A276/A276M S32205 vs EN 10088-1 X2CrNiMoN22-5-3

Strong Match — 87.8% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S32205 (ASTM A276/A276M:2017) and EN 10088-1 X2CrNiMoN22-5-3 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S32205 is defined under ASTM International, originating from United States, while EN 10088-1 X2CrNiMoN22-5-3 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S32205 vs EN 10088-1 X2CrNiMoN22-5-3 is a 87.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 87.8%.

Frequently Compared With ASTM A276/A276M S32205:
ASTM A959 2205 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH ASTM A959 255 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006
Match Breakdown
CHEMISTRY MATCH
87.8%
MECHANICAL MATCH
No shared data
OVERALL
87.8%
Specifications
Property ASTM A276/A276M S32205 EN 10088-1 X2CrNiMoN22-5-3
Standard ASTM A276/A276M:2017 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) <=2.00 <=2.00
P (%) <=0.030 <=0.035
S (%) <=0.020 <=0.015
Si (%) <=1.00 <=1.00
Cr (%) 22.0-23.0 21.0-23.0
Ni (%) 4.5-6.5 4.5-6.5
Mo (%) 3.0-3.5 2.50-3.5
N (%) 0.14-0.20 0.10-0.22
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S32205 EN 10088-1 X2CrNiMoN22-5-3
Tensile Strength >=655 MPa Not specified
Yield Strength >=450 MPa Not specified
Elongation >=25% Not specified
Hardness <=290 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S32205
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 X2CrNiMoN22-5-3
Not documented
Can ASTM A276/A276M S32205 Be Substituted With EN 10088-1 X2CrNiMoN22-5-3?
ASTM A276/A276M S32205 and EN 10088-1 X2CrNiMoN22-5-3 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMoN22-5-3 is often considered as a substitute for ASTM A276/A276M S32205 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M S32205
0 active listings and RFQs →
EN 10088-1 X2CrNiMoN22-5-3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S32205 and EN 10088-1 X2CrNiMoN22-5-3?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S32205 be substituted with EN 10088-1 X2CrNiMoN22-5-3?
ASTM A276/A276M S32205 and EN 10088-1 X2CrNiMoN22-5-3 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMoN22-5-3 is often considered as a substitute for ASTM A276/A276M S32205 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.