Minimal Match — 40% match
based on chemical composition and mechanical property overlap.
ASTM A276/A276M S32654 (ASTM A276/A276M:2017) and EN 10088-1 1.4401 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A276/A276M S32654 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-1 1.4401 is commonly used for marine, chemical processing, pharmaceutical equipment.
ASTM A276/A276M S32654 is defined under ASTM International, originating from United States, while EN 10088-1 1.4401 is defined under European Standard (EN), originating from Europe.
As per chemical composition, ASTM A276/A276M S32654 vs EN 10088-1 1.4401 is a 47.5% match.
As per mechanical properties, the match is 25%.
Combined, this makes them a minimal match overall at 40%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A276/A276M S32654
EN 10088-1 1.4401
Tensile Strength
>=750 MPa
≥520 MPa
Yield Strength
>=430 MPa
≥210 MPa
Elongation
>=40%
≥40%
Hardness
<=250 HB
≤215 HB
Condition
Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Not specified
Typical Applications
ASTM A276/A276M S32654
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 1.4401
Marine, chemical processing, pharmaceutical equipment
Key Differences
ASTM A276/A276M S32654 specifies P, S, N, Cu which are not specified for EN 10088-1 1.4401.
Can ASTM A276/A276M S32654 Be Substituted With EN 10088-1 1.4401?
ASTM A276/A276M S32654 and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between ASTM A276/A276M S32654 and EN 10088-1 1.4401?
ASTM A276/A276M S32654 specifies P, S, N, Cu which are not specified for EN 10088-1 1.4401.
Can ASTM A276/A276M S32654 be substituted with EN 10088-1 1.4401?
ASTM A276/A276M S32654 and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.