ASTM A276/A276M:2017 S32654 Steel: Specifications & Listings

ASTM A276/A276M:2017 S32654: S32654: austenitic stainless steel bars and shapes (UNS number, no type name printed). Specified in ASTM A276/A276M:2017.

Category: Stainless Steel
Grade Details
GradeASTM A276/A276M:2017 S32654
Standard ASTM A276/A276M:2017
ApplicationsStainless steel bars and shapes (hot-finished or cold-finished)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ASTM A959 S32654 ASTM A959:2011 USA No activity yet
EN 10088-1 X1CrNiMoCuN24-22-8 EN 10088-1:2014 Europe (CEN) No activity yet
IS 6603 X01Cr24Ni22Mo7CuN IS 6603:2024 India No activity yet
EN 10088-2 X1CrNiMoCuN24-22-8 EN 10088-2:2014 Europe No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
ASTM A959 S32654 ASTM A959:2011 Strong Match
ASTM A240/A240M S32654 ASTM A240/A240M:2025 Strong Match
EN 10088-1 X1CrNiMoCuN24-22-8 EN 10088-1:2014 Strong Match
EN 10088-1 X1CrNiMoCuN24-22-8 EN 10088-1:2023 Strong Match
IS 6603 X01Cr24Ni22Mo7CuN IS 6603:2024 Strong Match
EN 10088-2 X1CrNiMoCuN24-22-8 EN 10088-2:2014 Strong Match
EN 10088-3 X1CrNiMoCuN24-22-8 EN 10088-3:2014 Close Alternative
EN 10088-1 X1CrNiMoN25-22-2 EN 10088-1:2014 Related Material
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Mn P S Si Cr Ni Mo N Cu
<=0.020 2.0-4.0 <=0.030 <=0.005 <=0.50 24.0-25.0 21.0-23.0 7.0-8.0 0.45-0.55 0.30-0.60
Mechanical Properties
Tensile Strength >=750 MPa
Yield Strength >=430 MPa
Elongation >=40%
Hardness <=250 HB
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)

More data from ASTM A276/A276M:2017

From the standard
Mechanical requirements by condition and size 1 row(s)
ConditionFinishDiameter or thickness, in. [mm]Tensile strength, min (MPa)Yield strength, min (MPa)Elongation, min (%)Reduction of area, min (%)Brinell HBW, max
A (Annealed)hot-finished or cold-finishedall7504304040250
Yield by the 0.2 percent offset method. Hardness is HBW unless otherwise indicated; equivalent Rockwell is permitted.
Source: ASTM A276/A276M:2017, Table 2

Active ASTM A276/A276M:2017 S32654 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active ASTM A276/A276M:2017 S32654 listings at this time.

Register for Alerts

Buyer RFQs for ASTM A276/A276M:2017 S32654

+ Post an RFQ for this grade

No open buyer requirements for ASTM A276/A276M:2017 S32654 at this time.

Register for Alerts