ASTM A276/A276M S41425 vs ASTM A959 S41500

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S41425 (ASTM A276/A276M:2017) and ASTM A959 S41500 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S41425 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A959 S41500 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A276/A276M S41425 is defined under ASTM International, originating from United States, while ASTM A959 S41500 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M S41425 vs ASTM A959 S41500 is a 71.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A276/A276M S41425:
IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
71.3%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property ASTM A276/A276M S41425 ASTM A959 S41500
Standard ASTM A276/A276M:2017 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.05 <=0.05
Mn (%) 0.50-1.00 0.50-1.00
P (%) <=0.020 <=0.030
S (%) <=0.005 <=0.030
Si (%) <=0.50 <=0.60
Cr (%) 12.0-15.0 11.5-14.0
Ni (%) 4.0-7.0 3.5-5.5
Mo (%) 1.50-2.00 0.50-1.00
N (%) 0.06-0.12 Not specified
Cu (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S41425 ASTM A959 S41500
Tensile Strength >=825 MPa Not specified
Yield Strength >=655 MPa Not specified
Elongation >=15% Not specified
Hardness <=321 HB Not specified
Condition Condition T (Hardened and tempered, higher temperature), hot-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S41425
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A959 S41500
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A276/A276M S41425 Be Substituted With ASTM A959 S41500?
ASTM A276/A276M S41425 and ASTM A959 S41500 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S41425
0 active listings and RFQs →
ASTM A959 S41500
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S41425 and ASTM A959 S41500?
ASTM A276/A276M S41425 specifies N, Cu which are not specified for ASTM A959 S41500.
Can ASTM A276/A276M S41425 be substituted with ASTM A959 S41500?
ASTM A276/A276M S41425 and ASTM A959 S41500 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.