ASTM A276/A276M S41425 vs EN 10088-1 X3CrNiMoN27-5-2

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S41425 (ASTM A276/A276M:2017) and EN 10088-1 X3CrNiMoN27-5-2 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S41425 is defined under ASTM International, originating from United States, while EN 10088-1 X3CrNiMoN27-5-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S41425 vs EN 10088-1 X3CrNiMoN27-5-2 is a 70.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A276/A276M S41425:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
70.9%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property ASTM A276/A276M S41425 EN 10088-1 X3CrNiMoN27-5-2
Standard ASTM A276/A276M:2017 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.05 <=0.05
Mn (%) 0.50-1.00 <=2.00
P (%) <=0.020 <=0.035
S (%) <=0.005 <=0.015
Si (%) <=0.50 <=1.00
Cr (%) 12.0-15.0 25.0-28.0
Ni (%) 4.0-7.0 4.5-6.5
Mo (%) 1.50-2.00 1.30-2.00
N (%) 0.06-0.12 0.05-0.20
Cu (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S41425 EN 10088-1 X3CrNiMoN27-5-2
Tensile Strength >=825 MPa Not specified
Yield Strength >=655 MPa Not specified
Elongation >=15% Not specified
Hardness <=321 HB Not specified
Condition Condition T (Hardened and tempered, higher temperature), hot-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S41425
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 X3CrNiMoN27-5-2
Not documented
Key Differences
Can ASTM A276/A276M S41425 Be Substituted With EN 10088-1 X3CrNiMoN27-5-2?
ASTM A276/A276M S41425 and EN 10088-1 X3CrNiMoN27-5-2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S41425
0 active listings and RFQs →
EN 10088-1 X3CrNiMoN27-5-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S41425 and EN 10088-1 X3CrNiMoN27-5-2?
ASTM A276/A276M S41425 specifies Cu which is not specified for EN 10088-1 X3CrNiMoN27-5-2.
Can ASTM A276/A276M S41425 be substituted with EN 10088-1 X3CrNiMoN27-5-2?
ASTM A276/A276M S41425 and EN 10088-1 X3CrNiMoN27-5-2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.