ASTM A276/A276M S41500 vs ASTM A959 S41425

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S41500 (ASTM A276/A276M:2017) and ASTM A959 S41425 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S41500 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A959 S41425 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A276/A276M S41500 is defined under ASTM International, originating from United States, while ASTM A959 S41425 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M S41500 vs ASTM A959 S41425 is a 71.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A276/A276M S41500:
ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H ASTM A959 25-4-4 GOST 5632 06Kh23N28
Match Breakdown
CHEMISTRY MATCH
71.3%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property ASTM A276/A276M S41500 ASTM A959 S41425
Standard ASTM A276/A276M:2017 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.05 <=0.05
Mn (%) 0.50-1.00 0.50-1.00
P (%) <=0.030 <=0.020
S (%) <=0.030 <=0.005
Si (%) <=0.60 <=0.50
Cr (%) 11.5-14.0 12.0-15.0
Ni (%) 3.5-5.5 4.0-7.0
Mo (%) 0.50-1.00 1.50-2.00
Cu (%) Not specified <=0.30
N (%) Not specified 0.06-0.12
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S41500 ASTM A959 S41425
Tensile Strength >=795 MPa Not specified
Yield Strength >=620 MPa Not specified
Elongation >=15% Not specified
Hardness <=295 HB Not specified
Condition Condition T (Hardened and tempered, higher temperature), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S41500
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A959 S41425
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A276/A276M S41500 Be Substituted With ASTM A959 S41425?
ASTM A276/A276M S41500 and ASTM A959 S41425 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S41500
0 active listings and RFQs →
ASTM A959 S41425
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S41500 and ASTM A959 S41425?
ASTM A959 S41425 specifies Cu, N which are not specified for ASTM A276/A276M S41500.
Can ASTM A276/A276M S41500 be substituted with ASTM A959 S41425?
ASTM A276/A276M S41500 and ASTM A959 S41425 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.