ASTM A276/A276M S41500 vs EN 10088-1 X3CrNiMo13-4

Close Alternative — 76.1% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S41500 (ASTM A276/A276M:2017) and EN 10088-1 X3CrNiMo13-4 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S41500 is defined under ASTM International, originating from United States, while EN 10088-1 X3CrNiMo13-4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S41500 vs EN 10088-1 X3CrNiMo13-4 is a 76.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 76.1%.

Frequently Compared With ASTM A276/A276M S41500:
ASTM A959 .- EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH ASTM A959 25-4-4
Match Breakdown
CHEMISTRY MATCH
76.1%
MECHANICAL MATCH
No shared data
OVERALL
76.1%
Specifications
Property ASTM A276/A276M S41500 EN 10088-1 X3CrNiMo13-4
Standard ASTM A276/A276M:2017 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.05 <=0.05
Mn (%) 0.50-1.00 <=1.50
P (%) <=0.030 <=0.040
S (%) <=0.030 <=0.015
Si (%) <=0.60 <=0.70
Cr (%) 11.5-14.0 12.0-14.0
Ni (%) 3.5-5.5 3.5-4.5
Mo (%) 0.50-1.00 0.30-0.70
N (%) Not specified >=0.020
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S41500 EN 10088-1 X3CrNiMo13-4
Tensile Strength >=795 MPa Not specified
Yield Strength >=620 MPa Not specified
Elongation >=15% Not specified
Hardness <=295 HB Not specified
Condition Condition T (Hardened and tempered, higher temperature), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S41500
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 X3CrNiMo13-4
Not documented
Key Differences
Can ASTM A276/A276M S41500 Be Substituted With EN 10088-1 X3CrNiMo13-4?
ASTM A276/A276M S41500 and EN 10088-1 X3CrNiMo13-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A276/A276M S41500
0 active listings and RFQs →
EN 10088-1 X3CrNiMo13-4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S41500 and EN 10088-1 X3CrNiMo13-4?
EN 10088-1 X3CrNiMo13-4 specifies N which is not specified for ASTM A276/A276M S41500.
Can ASTM A276/A276M S41500 be substituted with EN 10088-1 X3CrNiMo13-4?
ASTM A276/A276M S41500 and EN 10088-1 X3CrNiMo13-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.