ASTM A276/A276M S42010 vs BS 970 (Part 1) 416S29

Related Material — 69.8% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S42010 (ASTM A276/A276M:2017) and BS 970 (Part 1) 416S29 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S42010 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while BS 970 (Part 1) 416S29 is commonly used for ferritic and martensitic stainless and heat resisting steel (section five). ASTM A276/A276M S42010 is defined under ASTM International, originating from United States, while BS 970 (Part 1) 416S29 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, ASTM A276/A276M S42010 vs BS 970 (Part 1) 416S29 is a 69.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.8%.

Frequently Compared With ASTM A276/A276M S42010:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
69.8%
MECHANICAL MATCH
No shared data
OVERALL
69.8%
Specifications
Property ASTM A276/A276M S42010 BS 970 (Part 1) 416S29
Standard ASTM A276/A276M:2017 BS 970 (Part 1):1991
Category Stainless Steel Stainless Steel
C (%) 0.15-0.30 0.14-0.20
Mn (%) <=1.00 <=1.5
P (%) <=0.040 <=0.060
S (%) <=0.030 0.15-0.35
Si (%) <=1.00 <=1.0
Cr (%) 13.5-15.0 11.5-13.5
Ni (%) 0.35-0.85 <=1.00
Mo (%) 0.40-0.85 <=0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S42010 BS 970 (Part 1) 416S29
Hardness <=235 HB Not specified
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S42010
Stainless steel bars and shapes (hot-finished or cold-finished)
BS 970 (Part 1) 416S29
Ferritic and martensitic stainless and heat resisting steel (section five)
Can ASTM A276/A276M S42010 Be Substituted With BS 970 (Part 1) 416S29?
ASTM A276/A276M S42010 and BS 970 (Part 1) 416S29 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S42010
0 active listings and RFQs →
BS 970 (Part 1) 416S29
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S42010 and BS 970 (Part 1) 416S29?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S42010 be substituted with BS 970 (Part 1) 416S29?
ASTM A276/A276M S42010 and BS 970 (Part 1) 416S29 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.