ASTM A276/A276M S43000 vs IS 1570 (Part 7) 12Cr13H
Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
ASTM A276/A276M S43000 (ASTM A276/A276M:2017) and IS 1570 (Part 7) 12Cr13H (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A276/A276M S43000 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while IS 1570 (Part 7) 12Cr13H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature.
ASTM A276/A276M S43000 is defined under ASTM International, originating from United States, while IS 1570 (Part 7) 12Cr13H is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, ASTM A276/A276M S43000 vs IS 1570 (Part 7) 12Cr13H is a 77.1% match.
As per mechanical properties, the match is 33.3%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A276/A276M S43000
IS 1570 (Part 7) 12Cr13H
Tensile Strength
>=415 MPa
470-670 MPa
Yield Strength
>=207 MPa
>=265 MPa (0.2 % proof stress)
Elongation
>=20%
>=20%
Condition
Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Bars, forgings, plates, A, thickness up to 160 (first row of Table 3)
Typical Applications
ASTM A276/A276M S43000
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 1570 (Part 7) 12Cr13H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
IS 1570 (Part 7) 12Cr13H specifies Ni which is not specified for ASTM A276/A276M S43000.
Can ASTM A276/A276M S43000 Be Substituted With IS 1570 (Part 7) 12Cr13H?
ASTM A276/A276M S43000 and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between ASTM A276/A276M S43000 and IS 1570 (Part 7) 12Cr13H?
IS 1570 (Part 7) 12Cr13H specifies Ni which is not specified for ASTM A276/A276M S43000.
Can ASTM A276/A276M S43000 be substituted with IS 1570 (Part 7) 12Cr13H?
ASTM A276/A276M S43000 and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.