ASTM A276/A276M S43000 vs ASTM A959 .-

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S43000 (ASTM A276/A276M:2017) and ASTM A959 .- (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S43000 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A959 .- is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A276/A276M S43000 is defined under ASTM International, originating from United States, while ASTM A959 .- is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M S43000 vs ASTM A959 .- is a 70.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A276/A276M S43000:
EN 10088-1 1.4006 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
70.1%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property ASTM A276/A276M S43000 ASTM A959 .-
Standard ASTM A276/A276M:2017 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.12 <=0.030
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cr (%) 16.0-18.0 18.0-20.0
Cb (%) Not specified 0.10-0.60
N (%) Not specified <=0.030
Ni (%) Not specified <=0.50
Ti (%) Not specified 0.07-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S43000 ASTM A959 .-
Tensile Strength >=415 MPa Not specified
Yield Strength >=207 MPa Not specified
Elongation >=20% Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S43000
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A959 .-
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A276/A276M S43000 Be Substituted With ASTM A959 .-?
ASTM A276/A276M S43000 and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S43000
0 active listings and RFQs →
ASTM A959 .-
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S43000 and ASTM A959 .-?
ASTM A959 .- specifies Cb, N, Ni, Ti which are not specified for ASTM A276/A276M S43000.
Can ASTM A276/A276M S43000 be substituted with ASTM A959 .-?
ASTM A276/A276M S43000 and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.