Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Mn
P
S
Si
Cr
Mo
0.95-1.20
<=1.00
<=0.040
<=0.030
<=1.00
16.0-18.0
<=0.75
Mechanical Properties
Hardness
<=269 HB
Condition
Condition A (Annealed), hot-finished, all sizes (first row printed)
More data from ASTM A276/A276M:2017
From the standard
Mechanical requirements by condition and size2 row(s)
Condition
Finish
Diameter or thickness, in. [mm]
Tensile strength, min (MPa)
Yield strength, min (MPa)
Elongation, min (%)
Reduction of area, min (%)
Brinell HBW, max
A (Annealed)
hot-finished
all
-
-
-
-
269
A (Annealed)
cold-finished
all
-
-
-
-
285
Yield by the 0.2 percent offset method. Hardness is HBW unless otherwise indicated; equivalent Rockwell is permitted.
Source: ASTM A276/A276M:2017, Table 2
Response to heat treatment3 values
Heat treatment temperature, min
1020 deg C (1875 deg F)
Quenchant
Air
Hardness after treatment, min
58 HRC
Test sample section not over 3/8 in. [9.50 mm] thick; temperature tolerance +/-14 deg C.
Source: ASTM A276/A276M:2017, Table 3