ASTM A276/A276M S44004 vs IS 11169 (Part 2) X04Cr17Mo1

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S44004 (ASTM A276/A276M:2017) and IS 11169 (Part 2) X04Cr17Mo1 (IS 11169 (Part 2):2023) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S44004 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while IS 11169 (Part 2) X04Cr17Mo1 is commonly used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, table 13). ASTM A276/A276M S44004 is defined under ASTM International, originating from United States, while IS 11169 (Part 2) X04Cr17Mo1 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A276/A276M S44004 vs IS 11169 (Part 2) X04Cr17Mo1 is a 83.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A276/A276M S44004:
IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301
Match Breakdown
CHEMISTRY MATCH
83.3%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property ASTM A276/A276M S44004 IS 11169 (Part 2) X04Cr17Mo1
Standard ASTM A276/A276M:2017 IS 11169 (Part 2):2023
Category Stainless Steel Stainless Steel
C (%) 0.95-1.20 <=0.08
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cr (%) 16.0-18.0 16.0-18.0
Mo (%) <=0.75 0.75-1.40
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S44004 IS 11169 (Part 2) X04Cr17Mo1
Hardness <=269 HB Not specified
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Not specified
Reduction of Area, soft annealed (+A) Not specified >=60% (over 5 to 25 mm)
Tensile Strength, soft annealed (+A) Not specified <=600 MPa (over 5 to 25 mm)
Typical Applications
ASTM A276/A276M S44004
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 11169 (Part 2) X04Cr17Mo1
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, Table 13)
Can ASTM A276/A276M S44004 Be Substituted With IS 11169 (Part 2) X04Cr17Mo1?
ASTM A276/A276M S44004 and IS 11169 (Part 2) X04Cr17Mo1 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S44004
0 active listings and RFQs →
IS 11169 (Part 2) X04Cr17Mo1
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S44004 and IS 11169 (Part 2) X04Cr17Mo1?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S44004 be substituted with IS 11169 (Part 2) X04Cr17Mo1?
ASTM A276/A276M S44004 and IS 11169 (Part 2) X04Cr17Mo1 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.