ASTM A516/A516M Grade 65 vs BS 970 (Part 3) 080M15

Strong Match — 85.5% match based on chemical composition and mechanical property overlap.

ASTM A516/A516M Grade 65 (ASTM A516/A516M:2025) and BS 970 (Part 3) 080M15 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Carbon Steel category. ASTM A516/A516M Grade 65 is typically used for welded pressure vessels where improved notch toughness is important, while BS 970 (Part 3) 080M15 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; carbon and carbon manganese steel (table 13). ASTM A516/A516M Grade 65 is defined under ASTM International, originating from United States, while BS 970 (Part 3) 080M15 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, ASTM A516/A516M Grade 65 vs BS 970 (Part 3) 080M15 is a 85.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 85.5%.

Frequently Compared With ASTM A516/A516M Grade 65:
BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 3) 070M20 BS 970 (Part 3) 080A15 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32 BS 970 (Part 1) 040A12
Match Breakdown
CHEMISTRY MATCH
85.5%
MECHANICAL MATCH
No shared data
OVERALL
85.5%
Specifications
Property ASTM A516/A516M Grade 65 BS 970 (Part 3) 080M15
Standard ASTM A516/A516M:2025 BS 970 (Part 3):1991
Category Carbon Steel Carbon Steel
C (%) <=0.24 0.12-0.18
Mn (%) 0.85-1.20 0.60-1.00
P (%) <=0.025 <=0.05
S (%) <=0.025 <=0.05
Si (%) 0.15-0.40 0.10-0.40
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A516/A516M Grade 65 BS 970 (Part 3) 080M15
Tensile Strength 450-585 MPa Not specified
Yield Strength >=240 MPa Not specified
Elongation >=19% Not specified
Condition Tension test per Table 2; one set of values for all thicknesses; plates 40 mm and under normally as-rolled, over 40 mm normalized; Elongation is in 200 mm gauge length, 50 mm values in the tensile block Not specified
Typical Applications
ASTM A516/A516M Grade 65
Welded pressure vessels where improved notch toughness is important
BS 970 (Part 3) 080M15
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; carbon and carbon manganese steel (Table 13)
Can ASTM A516/A516M Grade 65 Be Substituted With BS 970 (Part 3) 080M15?
ASTM A516/A516M Grade 65 and BS 970 (Part 3) 080M15 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 080M15 is often considered as a substitute for ASTM A516/A516M Grade 65 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A516/A516M Grade 65
0 active listings and RFQs →
BS 970 (Part 3) 080M15
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A516/A516M Grade 65 and BS 970 (Part 3) 080M15?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A516/A516M Grade 65 be substituted with BS 970 (Part 3) 080M15?
ASTM A516/A516M Grade 65 and BS 970 (Part 3) 080M15 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 080M15 is often considered as a substitute for ASTM A516/A516M Grade 65 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.