ASTM A588 Grade A vs AS/NZS 3678 Grade 350WR

Minimal Match — 53.8% match based on chemical composition and mechanical property overlap.

ASTM A588 Grade A (ASTM A588) and AS/NZS 3678 Grade 350WR (AS/NZS 3678:2016) are both steel grades. Both fall under the Structural Steel (Corten / Weathering) category. ASTM A588 Grade A is typically used for high-strength low-alloy structural steel with atmospheric corrosion resistance (weathering steel); bridges, transmission/communication towers, gusset plates, exposed structural applications, while AS/NZS 3678 Grade 350WR is commonly used for weather-resistant (corrosion-resistant) structural steel; exposed bridge and structural applications requiring atmospheric corrosion resistance. ASTM A588 Grade A is defined under ASTM International, originating from United States, while AS/NZS 3678 Grade 350WR is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, ASTM A588 Grade A vs AS/NZS 3678 Grade 350WR is a 80.7% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 53.8%.

Frequently Compared With ASTM A588 Grade A:
ASTM A588 CSA G40.21 50W JIS G3114 SMA400 CSA G40.21 260WT CSA G40.21 350A EN 10025-5 S355J2W EN 10025-5 S355J2WP EN 10025-5 S355J0WP CSA G40.21 480A ASTM A709 Grade HPS 70W ASTM A588 Grade B EN 10025-5 S235J2W
Match Breakdown
CHEMISTRY MATCH
80.7%
MECHANICAL MATCH
0%
OVERALL
53.8%
Specifications
Property ASTM A588 Grade A AS/NZS 3678 Grade 350WR
Standard ASTM A588 AS/NZS 3678:2016
Category Structural Steel (Corten / Weathering) Structural Steel (Corten / Weathering)
C (%) <=0.19 <=0.20
Mn (%) 0.80-1.25 <=1.70
Si (%) 0.30-0.65 <=0.50
P (%) <=0.040 <=0.035
S (%) <=0.050 <=0.035
Cu (%) 0.25-0.40 0.25-0.55
Cr (%) 0.40-0.65 0.40-0.80
Ni (%) <=0.40 <=0.65
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A588 Grade A AS/NZS 3678 Grade 350WR
Tensile Strength 485 MPa min 480-620 MPa
Yield Strength 345 MPa min 350 MPa min
Elongation 18% min 20% min
Hardness 140-190 HB Not specified
Typical Applications
ASTM A588 Grade A
High-strength low-alloy structural steel with atmospheric corrosion resistance (weathering steel); bridges, transmission/communication towers, gusset plates, exposed structural applications
AS/NZS 3678 Grade 350WR
Weather-resistant (corrosion-resistant) structural steel; exposed bridge and structural applications requiring atmospheric corrosion resistance
Can ASTM A588 Grade A Be Substituted With AS/NZS 3678 Grade 350WR?
ASTM A588 Grade A and AS/NZS 3678 Grade 350WR share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A588 Grade A
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2500–2700 mm (98.43–106.3 in)
AS/NZS 3678 Grade 350WR
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2500–2800 mm (98.43–110.24 in)
On M-EX Right Now
ASTM A588 Grade A
2 active listings and RFQs →
AS/NZS 3678 Grade 350WR
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A588 Grade A and AS/NZS 3678 Grade 350WR?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A588 Grade A be substituted with AS/NZS 3678 Grade 350WR?
ASTM A588 Grade A and AS/NZS 3678 Grade 350WR share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.