ASTM A588 Grade B vs ASTM A709 Grade HPS 70W

Minimal Match — 48.5% match based on chemical composition and mechanical property overlap.

ASTM A588 Grade B (ASTM A588) and ASTM A709 Grade HPS 70W (ASTM A709) are both steel grades. Both fall under the Structural Steel (Corten / Weathering) category. ASTM A588 Grade B is typically used for high-strength low-alloy structural steel with atmospheric corrosion resistance (weathering steel); bridges, transmission/communication towers, gusset plates, exposed structural applications, while ASTM A709 Grade HPS 70W is commonly used for high-performance steel (hps) with enhanced atmospheric corrosion resistance and toughness; primary bridge girders and structural members in bridge construction. ASTM A588 Grade B is defined under ASTM International, originating from United States, while ASTM A709 Grade HPS 70W is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A588 Grade B vs ASTM A709 Grade HPS 70W is a 69.1% match. As per mechanical properties, the match is 7.1%. Combined, this makes them a minimal match overall at 48.5%.

Frequently Compared With ASTM A588 Grade B:
ASTM A588 EN 10025-5 S355J2W EN 10025-5 S355J0WP JIS G3114 SMA400 CSA G40.21 260WT ASTM A588 Grade A CSA G40.21 350A CSA G40.21 50W AS/NZS 3678 Grade 350WR EN 10025-5 S355J2WP CSA G40.21 480A EN 10025-5 S235J2W
Match Breakdown
CHEMISTRY MATCH
69.1%
MECHANICAL MATCH
7.1%
OVERALL
48.5%
Specifications
Property ASTM A588 Grade B ASTM A709 Grade HPS 70W
Standard ASTM A588 ASTM A709
Category Structural Steel (Corten / Weathering) Structural Steel (Corten / Weathering)
C (%) <=0.20 <=0.11
Mn (%) 0.75-1.25 1.10-1.35
Si (%) 0.15-0.30 0.30-0.50
P (%) <=0.040 <=0.020
S (%) <=0.050 <=0.006
Cu (%) 0.20-0.40 0.25-0.40
Cr (%) 0.40-0.70 0.45-0.70
Ni (%) <=0.50 0.70-1.00
Mo (%) 0.02-0.10 0.02-0.08
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A588 Grade B ASTM A709 Grade HPS 70W
Tensile Strength 485 MPa min 585 MPa min
Yield Strength 345 MPa min 485 MPa min
Elongation 18% min 19% min
Hardness 140-190 HB 170-210 HB
Typical Applications
ASTM A588 Grade B
High-strength low-alloy structural steel with atmospheric corrosion resistance (weathering steel); bridges, transmission/communication towers, gusset plates, exposed structural applications
ASTM A709 Grade HPS 70W
High-performance steel (HPS) with enhanced atmospheric corrosion resistance and toughness; primary bridge girders and structural members in bridge construction
Can ASTM A588 Grade B Be Substituted With ASTM A709 Grade HPS 70W?
ASTM A588 Grade B and ASTM A709 Grade HPS 70W share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A588 Grade B
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 3100–3200 mm (122.05–125.98 in)
ASTM A709 Grade HPS 70W
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2500–3800 mm (98.43–149.61 in)
On M-EX Right Now
ASTM A588 Grade B
2 active listings and RFQs →
ASTM A709 Grade HPS 70W
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A588 Grade B and ASTM A709 Grade HPS 70W?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A588 Grade B be substituted with ASTM A709 Grade HPS 70W?
ASTM A588 Grade B and ASTM A709 Grade HPS 70W share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.