Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Mn
P
S
Si
Cr
V
Mo
Ni
0.45-0.55
0.20-0.50
<=0.030
<=0.030
0.95-1.15
4.75-5.50
0.80-1.40
1.30-1.80
1.25-1.75
Mechanical Properties
Hardness
<=248 HB
Condition
Annealed (maximum Brinell hardness)
More data from ASTM A681:2008
From the standard
Maximum hardness in delivery condition2 conditions
Condition
Maximum hardness (HB)
Annealed
248
Cold drawn
262
Maximum Brinell hardness (BHN).
Source: A681:2008, Table 2
Heat treatment and response to hardeninghardening test conditions
Preheat temperature
1450 deg F (788 deg C)
Austenitizing, salt bath
1825 deg F (996 deg C)
Austenitizing, controlled atmosphere furnace
1850 deg F (1010 deg C)
Austenitizing time
5 to 15 min
Quench medium
Air
Tempering temperature
950 deg F (510 deg C)
Minimum hardness after treatment
56 HRC
Austenitizing temperatures are stipulated for the response to hardening test only.
Source: A681:2008, Table 3