ASTM A681 H22 vs ASTM A681 H14

Close Alternative — 76.4% match based on chemical composition and mechanical property overlap.

ASTM A681 H22 (ASTM A681:2008) and ASTM A681 H14 (ASTM A681:2008) are both steel grades. Both fall under the Tool & Die Steels category. ASTM A681 H22 is typically used for tools, dies and fixtures (clause 1.2), while ASTM A681 H14 is commonly used for tools, dies and fixtures (clause 1.2). ASTM A681 H22 is defined under ASTM International, originating from United States, while ASTM A681 H14 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A681 H22 vs ASTM A681 H14 is a 64.6% match. As per mechanical properties, the match is 100%. Combined, this makes them a close alternative overall at 76.4%.

Frequently Compared With ASTM A681 H22:
DIN EN ISO 4957 1.2344 IS 1570 (Part 6) 103T3 GB/T 1299 3Cr2W8V IS 1570 (Part 6) 118T3 GB/T 1299 4Cr5MoSiV1 GOST 5950 4H5MFS GOST 5950 4H5MFS1 EN ISO 4957 1.2316 DIN EN ISO 4957 1.2379 GOST 5950 3H2W8F GB/T 1299 4Cr5MoSiV EN ISO 683-17 100Cr6
Match Breakdown
CHEMISTRY MATCH
64.6%
MECHANICAL MATCH
100%
OVERALL
76.4%
Specifications
Property ASTM A681 H22 ASTM A681 H14
Standard ASTM A681:2008 ASTM A681:2008
Category Tool & Die Steels Tool & Die Steels
C (%) 0.30-0.40 0.35-0.45
Mn (%) 0.15-0.40 0.20-0.60
P (%) <=0.030 <=0.030
S (%) <=0.030 <=0.030
Si (%) 0.15-0.40 0.80-1.25
Cr (%) 1.75-3.75 4.75-5.50
V (%) 0.25-0.50 Not specified
W (%) 10.00-11.75 4.00-5.25
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A681 H22 ASTM A681 H14
Hardness <=235 HB <=235 HB
Condition Annealed (maximum Brinell hardness) Annealed (maximum Brinell hardness)
Typical Applications
ASTM A681 H22
Tools, dies and fixtures (clause 1.2)
ASTM A681 H14
Tools, dies and fixtures (clause 1.2)
Key Differences
Can ASTM A681 H22 Be Substituted With ASTM A681 H14?
ASTM A681 H22 and ASTM A681 H14 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A681 H22
0 active listings and RFQs →
ASTM A681 H14
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A681 H22 and ASTM A681 H14?
ASTM A681 H22 specifies V which is not specified for ASTM A681 H14.
Can ASTM A681 H22 be substituted with ASTM A681 H14?
ASTM A681 H22 and ASTM A681 H14 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.