ASTM A681 H43 vs ASTM A681 H11

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A681 H43 (ASTM A681:2008) and ASTM A681 H11 (ASTM A681:2008) are both steel grades. Both fall under the Tool & Die Steels category. ASTM A681 H43 is typically used for tools, dies and fixtures (clause 1.2), while ASTM A681 H11 is commonly used for die casting dies, extrusion tooling, forging dies. ASTM A681 H43 is defined under ASTM International, originating from United States, while ASTM A681 H11 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A681 H43 vs ASTM A681 H11 is a 61.9% match. As per mechanical properties, the match is 100%. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A681 H43:
IS 1570 (Part 6) 133T3 EN ISO 4957 1.2316 EN ISO 683-17 100Cr6 GB/T 1299 3Cr2W8V GOST 5950 4H5MFS DIN EN ISO 4957 1.2344 DIN EN ISO 4957 1.2379 IS 1570 (Part 6) 103T3 IS 1570 (Part 6) 118T3 GOST 5950 3H2W8F GB/T 1299 4Cr5MoSiV GB/T 1299 4Cr5MoSiV1
Match Breakdown
CHEMISTRY MATCH
61.9%
MECHANICAL MATCH
100%
OVERALL
69.9%
Specifications
Property ASTM A681 H43 ASTM A681 H11
Standard ASTM A681:2008 ASTM A681:2008
Category Tool & Die Steels Tool & Die Steels
C (%) 0.50-0.65 0.33-0.43
Mn (%) 0.15-0.40 0.20-0.60
P (%) <=0.030 <=0.030
S (%) <=0.030 <=0.030
Si (%) 0.20-0.45 0.80-1.25
Cr (%) 3.75-4.50 4.75-5.50
V (%) 1.80-2.20 0.30-0.60
Mo (%) 7.75-8.50 1.10-1.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A681 H43 ASTM A681 H11
Hardness <=235 HB <=235 HB
Condition Annealed (maximum Brinell hardness) Annealed (maximum Brinell hardness)
Typical Applications
ASTM A681 H43
Tools, dies and fixtures (clause 1.2)
ASTM A681 H11
Die casting dies, extrusion tooling, forging dies
Can ASTM A681 H43 Be Substituted With ASTM A681 H11?
ASTM A681 H43 and ASTM A681 H11 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A681 H43
No active listings currently.
ASTM A681 H11
Flat Bar → (3 listings)
Thickness: 40–40 mm (1.57–1.57 in)
Width: 180–180 mm (7.09–7.09 in)
Length: 2500–4000 mm (98.43–157.48 in)
On M-EX Right Now
ASTM A681 H43
0 active listings and RFQs →
ASTM A681 H11
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A681 H43 and ASTM A681 H11?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A681 H43 be substituted with ASTM A681 H11?
ASTM A681 H43 and ASTM A681 H11 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.