Chemical Composition (%)
C
Mn
P
S
Si
Cr
V
Mo
0.33-0.43
0.20-0.60
<=0.030
<=0.030
0.80-1.25
4.75-5.50
0.30-0.60
1.10-1.60
Mechanical Properties
Hardness
<=235 HB
Condition
Annealed (maximum Brinell hardness)
Typical Available Sizes
Round Bar
16mm–400mm dia
Flat Bar
20×10mm–400×150mm
Square Bar
20mm–300mm
Sizes are indicative. Contact seller for exact availability.
More data from ASTM A681:2008
From the standard
Maximum hardness in delivery condition2 conditions
Condition
Maximum hardness (HB)
Annealed
235
Cold drawn
262
Maximum Brinell hardness (BHN).
Source: A681:2008, Table 2
Heat treatment and response to hardeninghardening test conditions
Preheat temperature
1450 deg F (788 deg C)
Austenitizing, salt bath
1825 deg F (996 deg C)
Austenitizing, controlled atmosphere furnace
1850 deg F (1010 deg C)
Austenitizing time
5 to 15 min
Quench medium
Air
Tempering temperature
1025 deg F (552 deg C)
Minimum hardness after treatment
53 HRC
Austenitizing temperatures are stipulated for the response to hardening test only.