ASTM A959 16-8-2H vs IS 11169 (Part 2) X04Cr17Ni12Mo2Ti

Close Alternative — 70.4% match based on chemical composition and mechanical property overlap.

ASTM A959 16-8-2H (ASTM A959:2011) and IS 11169 (Part 2) X04Cr17Ni12Mo2Ti (IS 11169 (Part 2):1989) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 16-8-2H is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 11169 (Part 2) X04Cr17Ni12Mo2Ti is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1). ASTM A959 16-8-2H is defined under ASTM International, originating from United States, while IS 11169 (Part 2) X04Cr17Ni12Mo2Ti is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 16-8-2H vs IS 11169 (Part 2) X04Cr17Ni12Mo2Ti is a 70.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 70.4%.

Frequently Compared With ASTM A959 16-8-2H:
ASTM A959 .- GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 08X18H10 EN 10088-1 1.4845 GOST 5632 06Kh23N28 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH EN 10088-1 1.4301 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
70.4%
MECHANICAL MATCH
No shared data
OVERALL
70.4%
Specifications
Property ASTM A959 16-8-2H IS 11169 (Part 2) X04Cr17Ni12Mo2Ti
Standard ASTM A959:2011 IS 11169 (Part 2):1989
Category Stainless Steel Stainless Steel
C (%) 0.05-0.10 <=0.08
Cr (%) 14.5-16.5 16.0-18.0
Mn (%) <=2.00 <=2.0
Mo (%) 1.50-2.00 2.0-3.0
Ni (%) 7.5-9.5 10.0-14.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Ti (%) Not specified >=5xC, <=0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 16-8-2H IS 11169 (Part 2) X04Cr17Ni12Mo2Ti
Yield Strength (0.2% proof) Not specified >=225 MPa
Tensile Strength Not specified 500-750 MPa
Elongation Not specified >=40%
Impact (U-notch 5 mm) Not specified >=60 J
Condition Not specified Quenched reference test piece (Table 6 treatment)
Typical Applications
ASTM A959 16-8-2H
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
Key Differences
Can ASTM A959 16-8-2H Be Substituted With IS 11169 (Part 2) X04Cr17Ni12Mo2Ti?
ASTM A959 16-8-2H and IS 11169 (Part 2) X04Cr17Ni12Mo2Ti are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 16-8-2H
0 active listings and RFQs →
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 16-8-2H and IS 11169 (Part 2) X04Cr17Ni12Mo2Ti?
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti specifies Ti which is not specified for ASTM A959 16-8-2H.
Can ASTM A959 16-8-2H be substituted with IS 11169 (Part 2) X04Cr17Ni12Mo2Ti?
ASTM A959 16-8-2H and IS 11169 (Part 2) X04Cr17Ni12Mo2Ti are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.