IS 11169 (Part 2):1989 X04Cr17Ni12Mo2Ti Steel: Specifications & Listings

IS 11169 (Part 2):1989 X04Cr17Ni12Mo2Ti: Cold heading quality austenitic stainless steel X04Cr17Ni12Mo2Ti to IS 11169 (Part 2):1989, supplied as wire, wire rod or bars and ordered on chemical composition alone or with mechanical properties. The standard was reaffirmed in 2004.

Category: Stainless Steel
Grade Details
GradeIS 11169 (Part 2):1989 X04Cr17Ni12Mo2Ti
Standard IS 11169 (Part 2):1989
ApplicationsCold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti IS 11169 (Part 2):2023 India No activity yet
IS 6911 X04Cr17Ni12Mo2Ti IS 6911:1992 India No activity yet
ASTM A959 316H ASTM A959:2011 USA No activity yet
ASTM A959 316Ti ASTM A959:2011 USA No activity yet
ASTM A959 316Cb ASTM A959:2011 USA No activity yet
BS 970 (Part 3) 316S33 BS 970 (Part 3):1991 UK No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
ASTM A959 SS316 ASTM A959:2011 Strong Match
ASTM A959 316Ti ASTM A959:2011 Strong Match
ASTM A959 316Cb ASTM A959:2011 Strong Match
ASTM A959 316H ASTM A959:2011 Strong Match
ASTM A959 316N ASTM A959:2011 Strong Match
BS 970 (Part 3) 320S31 BS 970 (Part 3):1991 Strong Match
BS 970 (Part 1) 320S31 BS 970 (Part 1):1983 Strong Match
BS 970 (Part 3) 316S31 BS 970 (Part 3):1991 Strong Match
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn Ni Cr Mo Ti S P
<=0.08 <=1.0 <=2.0 10.0-14.0 16.0-18.0 2.0-3.0 >=5xC, <=0.80 <=0.030 <=0.045
Mechanical Properties
Yield Strength (0.2% proof) >=225 MPa
Tensile Strength 500-750 MPa
Elongation >=40%
Impact (U-notch 5 mm) >=60 J
Condition Quenched reference test piece (Table 6 treatment)

More data from IS 11169 (Part 2):1989

From the standard
Properties in the delivery condition 3 conditions
Delivery conditionTensile strength, max (MPa)Reduction of area, min (%)
Quenched (Q), or quenched and peeled (Q+P)68055
Cold drawn and quenched (C+Q)68055
Cold drawn, quenched and lightly cold reduced (C+Q+LC)73055
Lightly cold reduced means, for example, a reduction of 5 percent. Table 4 prints the third condition as E+Q+LC; clause 10.2 gives C+Q+LC.
Source: IS 11169 (Part 2):1989, Table 4, clauses 8.1 and 10
Heat treatment of reference test pieces 1 value
Quenching temperature
1050 to 1100 °C
Treatment for the test pieces on which the mechanical properties are checked when ordered to requirement class 2 (clause 8.2).
Source: IS 11169 (Part 2):1989, Table 6

Active IS 11169 (Part 2):1989 X04Cr17Ni12Mo2Ti Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active IS 11169 (Part 2):1989 X04Cr17Ni12Mo2Ti listings at this time.

Register for Alerts

Buyer RFQs for IS 11169 (Part 2):1989 X04Cr17Ni12Mo2Ti

+ Post an RFQ for this grade

No open buyer requirements for IS 11169 (Part 2):1989 X04Cr17Ni12Mo2Ti at this time.

Register for Alerts