ASTM A959 2507 vs JIS G4304 SUS327L1

Strong Match — 100% match based on chemical composition and mechanical property overlap.

ASTM A959 2507 (ASTM A959:2011) and JIS G4304 SUS327L1 (JIS G4304:2021) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 2507 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while JIS G4304 SUS327L1 is commonly used for hot-rolled stainless steel plates and strips. ASTM A959 2507 is defined under ASTM International, originating from United States, while JIS G4304 SUS327L1 is defined under Japanese Industrial Standards (JIS), originating from Japan.

As per chemical composition, ASTM A959 2507 vs JIS G4304 SUS327L1 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With ASTM A959 2507:
ASTM A959 255 ASTM A959 25-4-4 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property ASTM A959 2507 JIS G4304 SUS327L1
Standard ASTM A959:2011 JIS G4304:2021
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 24.0-26.0 24.00-26.00
Cu (%) <=0.50 <=0.50
Mn (%) <=1.20 <=1.20
Mo (%) 3.0-5.0 3.00-5.00
N (%) 0.24-0.32 0.24-0.32
Ni (%) 6.0-8.0 6.00-8.00
P (%) <=0.035 <=0.035
S (%) <=0.020 <=0.020
Si (%) <=0.80 <=0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 2507 JIS G4304 SUS327L1
Tensile Strength Not specified >=795 MPa
Yield Strength Not specified >=550 MPa
Elongation Not specified >=15%
Hardness Not specified <=310 HB
Condition Not specified Solution heat treated plate and strip; proof strength applies only when specified by the purchaser
Typical Applications
ASTM A959 2507
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
JIS G4304 SUS327L1
Hot-rolled stainless steel plates and strips
Can ASTM A959 2507 Be Substituted With JIS G4304 SUS327L1?
ASTM A959 2507 and JIS G4304 SUS327L1 overlap closely enough on chemistry and mechanical properties that JIS G4304 SUS327L1 is often considered as a substitute for ASTM A959 2507 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 2507
0 active listings and RFQs →
JIS G4304 SUS327L1
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 2507 and JIS G4304 SUS327L1?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 2507 be substituted with JIS G4304 SUS327L1?
ASTM A959 2507 and JIS G4304 SUS327L1 overlap closely enough on chemistry and mechanical properties that JIS G4304 SUS327L1 is often considered as a substitute for ASTM A959 2507 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.