Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A959 304H (ASTM A959:2011) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 304H is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components. ASTM A959 304H is defined under ASTM International, originating from United States, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A959 304H vs EN 10088-1 1.4845 is a 63.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A959 304H:
GB/T 3280 06Cr19Ni10 ASTM A959 .- EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4301
Match Breakdown
CHEMISTRY MATCH
63.8%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property ASTM A959 304H EN 10088-1 1.4845
Standard ASTM A959:2011 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.04-0.10 ≤0.10
Cr (%) 18.0-20.0 24.0–26.0
Mn (%) <=2.00 ≤2.00
Ni (%) 8.0-11.0 19.0–22.0
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Si (%) <=1.00 ≤1.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 304H EN 10088-1 1.4845
Tensile Strength Not specified ≥515 MPa
Yield Strength Not specified ≥205 MPa
Elongation Not specified ≥40%
Max Service Temp Not specified 1100°C continuous
Typical Applications
ASTM A959 304H
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
Can ASTM A959 304H Be Substituted With EN 10088-1 1.4845?
ASTM A959 304H and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A959 304H
No active listings currently.
EN 10088-1 1.4845
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3200 mm (106.3–125.98 in)
On M-EX Right Now
ASTM A959 304H
0 active listings and RFQs →
EN 10088-1 1.4845
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 304H and EN 10088-1 1.4845?
ASTM A959 304H specifies P, S which are not specified for EN 10088-1 1.4845.
Can ASTM A959 304H be substituted with EN 10088-1 1.4845?
ASTM A959 304H and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.