ASTM A959 308 vs IS 11169 (Part 2) X04Cr18Ni10Ti

Strong Match — 88.9% match based on chemical composition and mechanical property overlap.

ASTM A959 308 (ASTM A959:2011) and IS 11169 (Part 2) X04Cr18Ni10Ti (IS 11169 (Part 2):1989) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 308 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 11169 (Part 2) X04Cr18Ni10Ti is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1). ASTM A959 308 is defined under ASTM International, originating from United States, while IS 11169 (Part 2) X04Cr18Ni10Ti is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 308 vs IS 11169 (Part 2) X04Cr18Ni10Ti is a 88.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 88.9%.

Frequently Compared With ASTM A959 308:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo EN 10088-1 1.4301
Match Breakdown
CHEMISTRY MATCH
88.9%
MECHANICAL MATCH
No shared data
OVERALL
88.9%
Specifications
Property ASTM A959 308 IS 11169 (Part 2) X04Cr18Ni10Ti
Standard ASTM A959:2011 IS 11169 (Part 2):1989
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Cr (%) 19.0-21.0 17.0-19.0
Mn (%) <=2.00 <=2.0
Ni (%) 10.0-12.0 9.0-12.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Ti (%) Not specified >=5xC, <=0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 308 IS 11169 (Part 2) X04Cr18Ni10Ti
Yield Strength (0.2% proof) Not specified >=205 MPa
Tensile Strength Not specified 500-750 MPa
Elongation Not specified >=40%
Impact (U-notch 5 mm) Not specified >=60 J
Condition Not specified Quenched reference test piece (Table 6 treatment)
Typical Applications
ASTM A959 308
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 11169 (Part 2) X04Cr18Ni10Ti
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
Key Differences
Can ASTM A959 308 Be Substituted With IS 11169 (Part 2) X04Cr18Ni10Ti?
ASTM A959 308 and IS 11169 (Part 2) X04Cr18Ni10Ti overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X04Cr18Ni10Ti is often considered as a substitute for ASTM A959 308 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 308
0 active listings and RFQs →
IS 11169 (Part 2) X04Cr18Ni10Ti
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 308 and IS 11169 (Part 2) X04Cr18Ni10Ti?
IS 11169 (Part 2) X04Cr18Ni10Ti specifies Ti which is not specified for ASTM A959 308.
Can ASTM A959 308 be substituted with IS 11169 (Part 2) X04Cr18Ni10Ti?
ASTM A959 308 and IS 11169 (Part 2) X04Cr18Ni10Ti overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X04Cr18Ni10Ti is often considered as a substitute for ASTM A959 308 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.