IS 11169 (Part 2):1989 X04Cr18Ni10Ti: Cold heading quality austenitic stainless steel X04Cr18Ni10Ti to IS 11169 (Part 2):1989, supplied as wire, wire rod or bars and ordered on chemical composition alone or with mechanical properties. Table 4 of the standard prints it as X04Cr18Ni10Ti2. The standard was reaffirmed in 2004.
| Grade | IS 11169 (Part 2):1989 X04Cr18Ni10Ti |
| Standard | IS 11169 (Part 2):1989 |
| Applications | Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1) |
| Grade | Standard | Match |
|---|---|---|
| ASTM A959 347 | ASTM A959:2011 | Strong Match |
| BS 970 (Part 3) 321S31 | BS 970 (Part 3):1991 | Strong Match |
| BS 970 (Part 3) 347S31 | BS 970 (Part 3):1991 | Strong Match |
| BS 970 (Part 1) 321S31 | BS 970 (Part 1):1983 | Strong Match |
| BS 970 (Part 1) 347S31 | BS 970 (Part 1):1983 | Strong Match |
| EN 10088-1 X6CrNiTi18-10 | EN 10088-1:2014 | Strong Match |
| EN 10088-1 X6CrNiNb18-10 | EN 10088-1:2014 | Strong Match |
| EN 10088-1 X6CrNiTi18-10 | EN 10088-1:2023 | Strong Match |
| C | Si | Mn | Ni | Cr | Ti | S | P |
|---|---|---|---|---|---|---|---|
| <=0.08 | <=1.0 | <=2.0 | 9.0-12.0 | 17.0-19.0 | >=5xC, <=0.80 | <=0.030 | <=0.045 |
| Yield Strength (0.2% proof) | >=205 MPa |
| Tensile Strength | 500-750 MPa |
| Elongation | >=40% |
| Impact (U-notch 5 mm) | >=60 J |
| Condition | Quenched reference test piece (Table 6 treatment) |
| Delivery condition | Tensile strength, max (MPa) | Reduction of area, min (%) |
|---|---|---|
| Quenched (Q), or quenched and peeled (Q+P) | 680 | 55 |
| Cold drawn and quenched (C+Q) | 680 | 55 |
| Cold drawn, quenched and lightly cold reduced (C+Q+LC) | 730 | 55 |