ASTM A959 310HCbN vs ASTM A959 310S

Strong Match — 89.4% match based on chemical composition and mechanical property overlap.

ASTM A959 310HCbN (ASTM A959:2011) and ASTM A959 310S (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 310HCbN is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A959 310S is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A959 310HCbN is defined under ASTM International, originating from United States, while ASTM A959 310S is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 310HCbN vs ASTM A959 310S is a 89.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 89.4%.

Frequently Compared With ASTM A959 310HCbN:
EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
89.4%
MECHANICAL MATCH
No shared data
OVERALL
89.4%
Specifications
Property ASTM A959 310HCbN ASTM A959 310S
Standard ASTM A959:2011 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) 0.04-0.10 <=0.08
Cb (%) 0.20-0.60 Not specified
Cr (%) 24.0-26.0 24.0-26.0
Mn (%) <=2.00 <=2.00
N (%) 0.15-0.35 Not specified
Ni (%) 19.0-22.0 19.0-22.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
ASTM A959 310HCbN
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A959 310S
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A959 310HCbN Be Substituted With ASTM A959 310S?
ASTM A959 310HCbN and ASTM A959 310S overlap closely enough on chemistry and mechanical properties that ASTM A959 310S is often considered as a substitute for ASTM A959 310HCbN in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 310HCbN
0 active listings and RFQs →
ASTM A959 310S
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 310HCbN and ASTM A959 310S?
ASTM A959 310HCbN specifies Cb, N which are not specified for ASTM A959 310S.
Can ASTM A959 310HCbN be substituted with ASTM A959 310S?
ASTM A959 310HCbN and ASTM A959 310S overlap closely enough on chemistry and mechanical properties that ASTM A959 310S is often considered as a substitute for ASTM A959 310HCbN in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.