Related Material — 61.2% match
based on chemical composition and mechanical property overlap.
ASTM A959 316H (ASTM A959:2011) and IS 1570 (Part 7) 12Cr12MoH (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A959 316H is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 1570 (Part 7) 12Cr12MoH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature.
ASTM A959 316H is defined under ASTM International, originating from United States, while IS 1570 (Part 7) 12Cr12MoH is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, ASTM A959 316H vs IS 1570 (Part 7) 12Cr12MoH is a 61.2% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 61.2%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A959 316H
IS 1570 (Part 7) 12Cr12MoH
Tensile Strength
Not specified
680-880 MPa
Yield Strength
Not specified
>=490 MPa (0.2 % proof stress)
Elongation
Not specified
>=20%
Condition
Not specified
Bars, forgings, Q+T, thickness up to 75 (first row of Table 3)
Typical Applications
ASTM A959 316H
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 1570 (Part 7) 12Cr12MoH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Can ASTM A959 316H Be Substituted With IS 1570 (Part 7) 12Cr12MoH?
ASTM A959 316H and IS 1570 (Part 7) 12Cr12MoH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between ASTM A959 316H and IS 1570 (Part 7) 12Cr12MoH?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 316H be substituted with IS 1570 (Part 7) 12Cr12MoH?
ASTM A959 316H and IS 1570 (Part 7) 12Cr12MoH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.