ASTM A959 316L vs IS 1570 (Part 5) X02Cr17Ni12Mo2

Strong Match — 100% match based on chemical composition and mechanical property overlap.

ASTM A959 316L (ASTM A959:2011) and IS 1570 (Part 5) X02Cr17Ni12Mo2 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 316L is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X02Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 316L vs IS 1570 (Part 5) X02Cr17Ni12Mo2 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With ASTM A959 316L:
EN 10088-1 1.4401 EN 10088-1 1.4006 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H ASTM A959 .- EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property ASTM A959 316L IS 1570 (Part 5) X02Cr17Ni12Mo2
Standard ASTM A959:2011 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 16.0-18.0 16.0-18.0
Mn (%) <=2.00 <=2.0
Mo (%) 2.00-3.00 2.0-3.0
Ni (%) 10.0-14.0 10.0-14.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 316L IS 1570 (Part 5) X02Cr17Ni12Mo2
Tensile Strength Not specified >=485 MPa
Yield Strength Not specified >=170 MPa (0.2 % proof stress)
Elongation Not specified >=40% (50 mm)
Hardness Not specified <=217 HB; <=95 HRB
Condition Not specified Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Typical Applications
ASTM A959 316L
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 1570 (Part 5) X02Cr17Ni12Mo2
Not documented
Can ASTM A959 316L Be Substituted With IS 1570 (Part 5) X02Cr17Ni12Mo2?
ASTM A959 316L and IS 1570 (Part 5) X02Cr17Ni12Mo2 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X02Cr17Ni12Mo2 is often considered as a substitute for ASTM A959 316L in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 316L
0 active listings and RFQs →
IS 1570 (Part 5) X02Cr17Ni12Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 316L and IS 1570 (Part 5) X02Cr17Ni12Mo2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 316L be substituted with IS 1570 (Part 5) X02Cr17Ni12Mo2?
ASTM A959 316L and IS 1570 (Part 5) X02Cr17Ni12Mo2 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X02Cr17Ni12Mo2 is often considered as a substitute for ASTM A959 316L in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.