Strong Match — 95.4% match
based on chemical composition and mechanical property overlap.
ASTM A959 430F (ASTM A959:2011) and IS 11169 (Part 2) X07Cr17 (IS 11169 (Part 2):1989) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A959 430F is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 11169 (Part 2) X07Cr17 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1).
ASTM A959 430F is defined under ASTM International, originating from United States, while IS 11169 (Part 2) X07Cr17 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, ASTM A959 430F vs IS 11169 (Part 2) X07Cr17 is a 95.4% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 95.4%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A959 430F
IS 11169 (Part 2) X07Cr17
Yield Strength (0.2% proof)
Not specified
>=270 MPa
Tensile Strength
Not specified
450-600 MPa
Elongation
Not specified
>=20%
Condition
Not specified
Annealed reference test piece (Table 6 treatment)
Typical Applications
ASTM A959 430F
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 11169 (Part 2) X07Cr17
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
Can ASTM A959 430F Be Substituted With IS 11169 (Part 2) X07Cr17?
ASTM A959 430F and IS 11169 (Part 2) X07Cr17 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X07Cr17 is often considered as a substitute for ASTM A959 430F in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between ASTM A959 430F and IS 11169 (Part 2) X07Cr17?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 430F be substituted with IS 11169 (Part 2) X07Cr17?
ASTM A959 430F and IS 11169 (Part 2) X07Cr17 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X07Cr17 is often considered as a substitute for ASTM A959 430F in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.