IS 11169 (Part 2):1989 X07Cr17: Cold heading quality ferritic stainless steel X07Cr17 to IS 11169 (Part 2):1989, supplied as wire, wire rod or bars and ordered on chemical composition alone or with mechanical properties. The standard was reaffirmed in 2004.

Category: Stainless Steel
Grade Details
GradeIS 11169 (Part 2):1989 X07Cr17
Standard IS 11169 (Part 2):1989
ApplicationsCold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
IS 6911 X07Cr17 IS 6911:1992 India No activity yet
ASTM A959 429 ASTM A959:2011 USA No activity yet
ASTM A959 430 ASTM A959:2011 USA No activity yet
ASTM A959 430F ASTM A959:2011 USA No activity yet
ASTM A959 430FSe ASTM A959:2011 USA No activity yet
EN 10088-1 X6Cr17 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-1 X10CrAlSi18 EN 10088-1:2014 Europe (CEN) No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
ASTM A959 430 ASTM A959:2011 Strong Match
ASTM A959 430FSe ASTM A959:2011 Strong Match
EN 10088-1 X6Cr17 EN 10088-1:2014 Strong Match
EN 10088-1 X6Cr17 EN 10088-1:2023 Strong Match
ASTM A959 430F ASTM A959:2011 Strong Match
ASTM A959 429 ASTM A959:2011 Strong Match
EN 10088-1 X10CrAlSi18 EN 10088-1:2014 Strong Match
EN 10088-1 X10CrAlSi18 EN 10088-1:2023 Strong Match
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn Cr S P
<=0.12 <=1.0 <=1.0 16.0-18.0 <=0.030 <=0.045
Mechanical Properties
Yield Strength (0.2% proof) >=270 MPa
Tensile Strength 450-600 MPa
Elongation >=20%
Condition Annealed reference test piece (Table 6 treatment)

More data from IS 11169 (Part 2):1989

From the standard
Properties in the delivery condition 3 conditions
Delivery conditionTensile strength, max (MPa)Reduction of area, min (%)
Annealed (AC), or annealed and peeled (AC+P)57063
Cold drawn and annealed (C+AC)57060
Cold drawn, annealed and lightly cold reduced (C+AC+LC)62065
Annealing is spheroidising annealing. Lightly cold reduced means, for example, a reduction of 5 percent.
Source: IS 11169 (Part 2):1989, Table 4, clauses 8.1 and 10
Heat treatment of reference test pieces 2 values
Annealing temperature
750 to 850 °C
Annealing, cooling
Air or water
Treatment for the test pieces on which the mechanical properties are checked when ordered to requirement class 2 (clause 8.2).
Source: IS 11169 (Part 2):1989, Table 6

Active IS 11169 (Part 2):1989 X07Cr17 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active IS 11169 (Part 2):1989 X07Cr17 listings at this time.

Register for Alerts

Buyer RFQs for IS 11169 (Part 2):1989 X07Cr17

+ Post an RFQ for this grade

No open buyer requirements for IS 11169 (Part 2):1989 X07Cr17 at this time.

Register for Alerts